Wei Xu,Chenjin Hou,Yuxuan Mao,Lei Yang,Maryam Tamaddon,Jianliang Zhang,Xuanhui Qu,Chaozong Liu,Bo Su,Xin Lu
Abstract:When biomaterials are implanted in the human body, the surfaces of the implants become favorable sites for microbial adhesion and biofilm formation, causing peri-implant infection which frequently results in the failure of prosthetics and revision surgery. Ti-Mo alloy is one of the commonly used implant materials for load-bearing bone replacement, and the prevention of infection of Ti-Mo implants is therefore crucial. In this study, bacterial inhibitory copper (Cu) was added to Ti-Mo matrix to develop a novel Ti-Mo-Cu alloy with bacterial inhibitory property. The effects of Cu content on microstructure, tensile properties, cytocompatibility, and bacterial inhibitory ability of Ti-Mo-Cu alloy were systematically investigated. Results revealed that Ti-10Mo-1Cu alloy consisted of α and β phases, while there were a few Ti<sub>2</sub>Cu intermetallic compounds existed for Ti-10Mo-3Cu and Ti-10Mo-5Cu alloys, in addition to α and β phases. The tensile strength of Ti-10Mo-xCu alloy increased with Cu content while elongation decreased. Ti-10Mo-3Cu alloy exhibited an optimal tensile strength of 1098.1 MPa and elongation of 5.2%. Cytocompatibility study indicated that none of the Ti-10Mo-xCu alloys had a negative effect on MC3T3-E1 cell proliferation. Bacterial inhibitory rates against <i>S. aureus</i> and <i>E. coli</i> increased with the increase in Cu content of Ti-10Mo-xCu alloy, within the ranges of 20-60% and 15-50%, respectively. Taken together, this study suggests that Ti-10Mo-3Cu alloy with high strength, acceptable elongation, excellent cytocompatibility, and the bacterial inhibitory property is a promising candidate for biomedical implant applications.
What problem does this paper attempt to address?
The problems that this paper attempts to solve mainly focus on the following aspects:
1. **Prevention of titanium alloy implant infections**: Titanium and its alloys are commonly used bone - substitute implant materials. However, these implants are likely to become favorable sites for microorganism adhesion and biofilm formation, leading to infections at the implant site, which often results in prosthesis failure and the need for revision surgery. Therefore, it is crucial to prevent infections of titanium alloy implants.
2. **Improvement of the antibacterial properties of titanium alloys**: In order to improve the antibacterial properties of titanium alloys, researchers added copper (Cu) with antibacterial characteristics to the Ti - 10Mo matrix and developed a new type of Ti - 10Mo - Cu alloy. Specifically, the researchers systematically studied the influence of Cu content on the microstructure, tensile properties, cell compatibility and antibacterial ability of the Ti - 10Mo - Cu alloy.
3. **Optimization of the comprehensive properties of the alloy**: By adding different amounts of Cu, the researchers hope to find an alloy with high strength, good ductility, excellent cell compatibility and antibacterial properties to meet the application requirements of biomedical implants.
### Research background
- **Advantages of titanium and its alloys**: Titanium and its alloys have attracted increasing attention in the fields of orthopedics and dentistry because of their excellent mechanical properties, corrosion resistance and biocompatibility.
- **Existing problems**: Although titanium and its alloys have many advantages, they also have some potential problems, such as the release of toxic aluminum (Al) or vanadium (V) ions, the mismatch of elastic modulus with bones resulting in the stress - shielding effect, and bacterial infections.
- **Development of new β - type titanium alloys**: In order to improve biocompatibility and reduce the stress - shielding effect, researchers have designed and developed many new β - type titanium alloys, such as Ti - Nb - Zr and Ti - Mo - based alloys. Among them, the Ti - Mo - based alloys containing 4 - 20% Mo have attracted wide attention because of their relatively low cost, high strength, low elastic modulus and excellent biocompatibility.
### Research methods
- **Material preparation**: Ti - 10Mo - xCu alloys with different Cu contents were prepared by powder metallurgy method using commercially pure Ti, Mo and Cu powders.
- **Microstructure characterization**: The microstructure of the alloys was characterized by X - ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM).
- **Mechanical property testing**: The tensile properties of the alloys were tested by tensile tests.
- **Cell compatibility testing**: The cell compatibility of the alloys was evaluated using mouse osteoblasts (MC3T3 - E1).
- **Antibacterial property testing**: The antibacterial properties of the alloys were evaluated by culturing Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli).
- **Copper ion release testing**: The amount of copper ion release of the alloys in deionized water was tested by inductively coupled plasma - mass spectrometry (ICP - MS).
### Main conclusions
- **Microstructure**: The Ti - 10Mo - 1Cu alloy is mainly composed of α and β phases, while the Ti - 10Mo - 3Cu and Ti - 10Mo - 5Cu alloys, in addition to α and β phases, also contain a small amount of Ti₂Cu intermetallic compounds.
- **Mechanical properties**: With the increase of Cu content, the tensile strength of the Ti - 10Mo - xCu alloys increases, while the elongation decreases. Among them, the Ti - 10Mo - 3Cu alloy exhibits the best tensile strength (1098.1 MPa) and elongation (5.2%).
- **Cell compatibility**: All Ti - 10Mo - xCu alloys did not have a negative impact on the proliferation of MC3T3 - E1 cells, and the cytotoxicity level was extremely low (grade 0).
- **Antibacterial properties**: With the increase of Cu content, the antibacterial rates of the Ti - 10Mo - xCu alloys against S. aureus and E. coli gradually increase between 20 - 60% and 15 - 50% respectively.
- **Comprehensive properties**: The Ti - 10Mo - 3Cu alloy has high strength, good ductility, excellent cell compatibility and antibacterial properties, and is a promising biomedical implant material.
In summary, through adding Cu to the Ti - 10Mo matrix, this research has successfully developed a new type of Ti - 10Mo - Cu alloy, which performs well in mechanical properties, cell compatibility and antibacterial properties, and is expected to be used in the application of biomedical implants.