Fabrication and Biological Evaluation of the Coating Co‐doped Strontium and Zinc Nanoparticles on Porous Pure Titanium Surface by Hydrothermal Method

Yanqi Chen,fuming he

DOI: https://doi.org/10.1111/clr.10_13509

2019-01-01

Clinical Oral Implants Research

Abstract:Background For dental implants, early infection and peri-implantitis after implant restoration are major reasons for implant failure. Plaque biofilm formation is the initiator for implant-related infection. Therefore, it is urgent to develop a new antibacterial implant materials or treatment methods. Aim/Hypothesis In this study, Sr- and Zn- incorporated micro nano-structured titanium surface with nanorods (MNT-Sr Zn) was fabricated by a two-step hydrothermal process, aiming to improve osseointegration and reduce implant failure caused by implant-related infection and broaden new ideas for the future research Material and Methods The Mod Ti surfaces were used as a control. The characterization of different surfaces was detected by a field emission scanning electron microscope (FE-SEM) equipped with energy dispersive spectra (EDS) detector, x-ray diffractometer (XRD) and inductively coupled plasma mass spectroscopy (ICP-MS). Meanwhile, Staphylococcus aureus (S. aureus) was selected to evaluate antibacterial properties through Live Dead Staining and watching the adhesive bacterial morphology under FE-SEM. What's more, rat bone marrow-derived mesenchymal stem cells (rBMSCs) were cultured on the surfaces to detect their early osteogenic properties, like the alkaline phosphatase(ALP) activity and the expressions of osteogenesis related genes. Results The results confirmed that nanorod-like particles with a diameter of about 30-50 nm of MNT-Sr Zn composed of well-crystallized ZnO and SrTiO3 phases. In the EDS spectra, the elements of Zn and Sr were evenly distributed, and approximately 1.49 ± 0.16 wt% and 21.69 ± 2.74 wt% respectively. Besides, the release of Sr2+ and Zn2+ was a controlled and long-term process. More importantly, Zn-containing nanorod-like particles and the morphology could work together, slightly decreasing adhesion of S. aureus but increasing the proportion of dead cells, thus inhibiting subsequent biofilm formation, compared with the controlled group. In addition to this, MNT-Sr Zn could enhance the osteogenic differentiation via the upregulation of the transcription of osteogenic related genes and the expression of ALP in vitro. Conclusion and Clinical Implications This research provides a new surface modification method on titanium substrate for multi-functional implant material development. Due to the co-doping of Sr and Zn in the coating, biomechanical stability, antibacterial capability and early osteogenic inductive effect are enhanced, which has the potential to be applied in dental implantation in the future.