Abstract:A high-temperature, high-cycle fatigue test was conducted on a nickel-based single-crystal superalloy with a pore structure. Optical and scanning electron microscopy were utilized to examine the crack propagation paths and fatigue fracture surfaces at the macro and micro scales. The analysis of crack initiation and propagation related to the pore structure facilitated the development of a crack shape factor reflecting these distinct fracture behaviors. Predictions about the high-cycle fatigue stress experienced by the specimen were made, accompanied by an error analysis, providing critical insights for precise stress calculations and structural optimization in engine blade design. The results reveal that high-cycle fatigue cracks originate from corner cracks at pore edges, with the initial propagation displaying smooth crystallographic plane features. Subsequent stages show clear fatigue arc patterns in the propagation zones. The fracture surface exhibits the significant layering of oxide layers, primarily composed of NiO, with traces of CoO displaying columnar growth. AL2O3 is predominantly found at the interfaces between the matrix and oxide layers. Short and straight dislocations near the oxide layers and within the matrix suggest that dislocation multiplication and planar slip dominate the slip mechanisms in this alloy. The orientation of the fracture surface is mainly perpendicular to the load direction, with minor inclined facets in localized areas. Correlations were established between the plastic zone dimensions at the crack tips and the corresponding fatigue stresses. Without grain boundaries in single-crystal alloys, these dimensions are easily derived as parameters for fatigue stress analysis. The selected crack shape factor, "elliptical corner crack at pore edges", captures the initiation and propagation traits relevant to porous structures. Subsequent calculations, accounting for the impact of oxide layers on stress assessments, indicated an error ratio ranging from 1.00 to 1.21 compared to nominal stress values.

A fatigue life prediction method distinguishing fracture modes for Ni-based single crystal superalloys considering porosity defect

The effect of porosity size on the high cycle fatigue life of nickel-based single crystal superalloy at 980 °C

A crystal plasticity-based approach for creep-fatigue life prediction and damage evaluation in a nickel-based superalloy

The effect of porosity size and oxidation on the HCF property of nickel-based single crystal superalloy at 980 °C

In-phase Thermomechanical Fatigue Lifetime Prediction of Nickel-Based Single Crystal Superalloys from Smooth Specimens to Notched Specimens Based on Coupling Damage on Critical Plane

A topologized resolved shear stress method for the life prediction of nickel-base single crystal superalloys

Low-cycle Fatigue Life Prediction of a Polycrystalline Nickel-Base Superalloy Using Crystal Plasticity Modelling Approach

High-Cycle Fatigue Fracture Behavior and Stress Prediction of Ni-Based Single-Crystal Superalloy with Film Cooling Hole Drilled Using Femtosecond Laser

Fatigue Life Prediction of Film-cooling Hole Specimens with Initial Damage

Fatigue Life Prediction of Nickel-Based GH4169 Alloy on the Basis of a Multi-Scale Crack Propagation Approach

The whole fatigue crack propagation life prediction of Ni-based single crystal super-alloy specimen with single hole based on EIFS and ‘Fish-eye’ theory

Damage-based Low Cycle Fatigue Lifetime Prediction of Nickel-Based Single Crystal Superalloy Considering Anisotropy and Dwell Types

A Low Cycle Fatigue Life Prediction Model Of Single Crystal Nickel-Based Superalloys Using Critical Plane Approach Combined With Crystallographic Slip Theory

Fatigue Life Assessment of a Porous Casting Nickel-Based Superalloy Based on Fracture Mechanics Methodology

Life prediction and damage analysis of creep-fatigue combined with high-low cycle loading by using a crystal plasticity-based approach

Fatigue Life Estimation of Nickel-Based Single Crystal Superalloy with Different Inclined Film Cooling Holes: Initial Damage Quantification and Coupling of Damage-Fracture Mechanics Models

Dislocation-based crystal plasticity modelling of a nickel-based superalloy under dwell-fatigue: From life prediction to residual life assessment

Fracture Mechanisms Induced by Microporosity and Precipitates in Isothermal Fatigue of Polycrystalline Nickel Based Superalloy

Creep-fatigue damage mechanisms and life prediction based on crystal plasticity combined with grain boundary cavity model in a nickel-based superalloy at 650°C

A fatigue life prediction approach for porosity defect-induced failures in directed energy deposited Ti-6Al-4V considering crack growth environment

The EIFS-based fatigue life prediction approach of nickel-based single crystals with film cooling holes at elevated temperature