Abstract:<p>Recently, binder jetting additive manufacturing (BJAM) was used to manufacture complex metal parts in an economical and large-scale way. However, the usage of resin to bond metal powder renders as-printed green parts with low strength, which is potential to cause the structural damages of final parts during post treatments. To overcome the intractable problem, a self-developed binder mainly consisting of A-stage phenolic resin was explored for BJAM to achieve relatively high-strength as-printed green parts. The binder can be cured as a C-stage phenolic resin with 190 ℃ and then provide a high strength for the green parts. The effect of layer thickness and binder saturation on the strength, dimensional accuracy, and surface roughness of the BJAM-printed 316 L stainless-steel green samples using the developed binder was investigated systematically. With the optimized parameters (a layer thickness of 100 μm and a binder saturation of 30.2%), green samples can possess the ultimate bending strength (UBS) of 10.08 MPa and the ultimate compressive strength (UCS) of 25.56 MPa, which are beneficial for the structural stability of the printed samples during subsequent treatments. A reduction in strength and an increase in roughness are observed with increasing the layer thickness for the as-printed green samples. An increment in binder saturation results in the improvement in strength and surface roughness of the green samples. The relationships between the binder and the mechanical performance of the green samples were discussed from the viewpoint of the uneven distribution of binder in depth. This work explored a promising binder with a low saturation for BJAM to fabricate 316 L green parts with desirable mechanical strength and acceptable surface roughness.</p>

Predictive Binder Jet Additive Manufacturing enabled by Clean Burn-off Binder Design

A Versatile Thermally Initiated Crosslinking Binder for Additive Manufacturing of Strong Structures

Process development for green part printing using binder jetting additive manufacturing

A thermal-initiated monomer binder enhancing green strength with low binder saturation for binder jetting additive manufacturing of cemented carbide

A Scalable and Universal Xerogel As Binder for Additive Manufacturing of Strong Structures

Overcoming the Penetration–saturation Trade-off in Binder Jet Additive Manufacturing Via Rapid in Situ Curing

Enhancing Quality Control: Image-Based Quantification of Carbides and Defect Remediation in Binder Jetting Additive Manufacturing

Binder jetting additive manufacturing of 316L stainless-steel green parts with high strength and low binder content: Binder preparation and process optimization

Metal Binder Jetting Additive Manufacturing: A Literature Review

Binder jet 3D printing—Process parameters, materials, properties, modeling, and challenges

State of the art of metal powder bonded binder jetting printing technology

A review on recent developments in binder jetting metal additive manufacturing: materials and process characteristics

Optimization of Binder Jetting Using Taguchi Method

Non-heat source forming technology of binder jetting metal powder and its post-treatment process

Additive manufacturing of carbon steel with site-specific compositions and properties using binder jetting and spark plasma sintering

Photopolymerization of Stainless Steel 420 Metal Suspension: Printing System and Process Development of Additive Manufacturing Technology toward High-Volume Production

Pressure‐assisted Binder Jetting for Additive Manufacturing of Mock Energetic Composites

Multi-objective optimization of binder jet additive manufacturing of Co-Cr-Mo using machine learning

Tailoring green and sintered density of pure iron parts using binder jetting additive manufacturing

Effect of feedstock bimodal powder design and cold isostatic pressing on the mechanical behavior of binder jetting additive manufactured Inconel 718 superalloy