Influence of heat treatment on the microstructure and creep response of additively manufactured cobalt superalloy Mar M509

V. KalyanasundaramS.R. HoldsworthY. PardhiC SoothillE. Hosseinia Empa Swiss Federal Laboratories for Materials Science & Technology,Dübendorf,Switzerlandb Sulzer Pumps,Leeds,West Yorkshire,UKc Sulzer Rotating Equipment Services,Winterthur,Switzerland
DOI: https://doi.org/10.1080/09603409.2024.2301853
2024-01-10
Materials at High Temperatures
Abstract:This work explores the influence of various post-build heat treatment procedures on the microstructural characteristics and creep response of laser powder bed fusion (L-PBF) Mar M509 superalloy. Besides MC-type carbides formed primarily during the L-PBF process, the obtained results indicate the influence of heat treatment on the nucleation of M 6 C and M 7 C 3 carbides due to elemental segregation. Short-term creep-rupture tests have been conducted at 900°C/110MPa on eight specimens, each subjected to a specifically individual heat treatment procedure. Rupture times are found to be sensitive to the heat treatment applied and vary from ~178 to ~641 hours. Detailed microscopic characterisation of ruptured specimens highlights the synergistic influence of oxidation and M 7 C 3 /M 6 C precipitate-free zone formation on macroscopic intergranular failure facilitated by grain boundary sliding along favourably oriented small grains. Besides notable grain growth, the presence of a serrated grain boundary structure with relatively less MC-type carbide coarsening is found to offer the best creep resistance among the eight L-PBF specimens. Further improvement of the elevated temperature performance of the alloy is seen to require a focus on the L-PBF process conditions to optimise the morphology of MC carbides, as they form.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?