Abstract:Silver coating in its jewelry application needs to resist tarnishing as well as wear. The corrosion and tribological behavior of pulse reverse current (PRC) and the addition of SiC 45-60 nm-size nanoparticles in the Ag-Ge coating on copper substrate were investigated. The contact angle, open circuit potential and electrochemical polarization in ammonium sulfide and artificial sweat media and thioacetamide corrosion were studied. Moreover, the pin-on-disc method and microhardness were used to assess the wear behavior of the coatings. FE-scanning electron microscopy equipped with energy dispersive spectroscopy and x-ray diffraction patterns were used. During reverse time in PRC process, the already reduced hydrogen on cathode surface was released and resulted in fine-grained microstructure, reduction of internal defects and smooth surface, which in turn improved the corrosion resistance of the coating. PRC together with nano-SiC changed the coating behavior from super-hydrophilic to hydrophobicity. Corrosion analysis showed that PRC sample possessed the best resistance to corrosion in both ammonium sulfide as well as artificial sweat. Although SiC addition reduced the corrosion resistance, still was much higher than that of direct current sample. Analyses of the wear behavior of the deposited film showed that samples containing SiC nanoparticles obtained superior wear resistance than samples without SiC. The dominant wear mechanism in both DC and PRC coatings was the delamination mechanism, whereas the wear mechanism in the coatings contained 4 and 8 g SiC in electrolyte was the adhesive wear mechanism.

Study of Ag Sb coatings prepared by non-cyanide electrodeposition

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

The Corrosion Behavior of Different Silver Plating Layers as Electrical Contact Materials in Sulfur-Containing Environments

A facile fabrication of Ag/SiC composite coating with high mechanical properties and corrosion resistance by electroless plating

Influence of Ag Contents on Structure and Tribological Properties of TiSiN-Ag Nanocomposite Coatings on Ti–6Al–4V

Effect of the impurity in electroless plated Powders on morphology and properties of sintered AgSnO2 materials

Sintering of the ultrafine Ag-SnO2 powders prepared by electroless silver plating

Anti-Arc Erosion Properties of Ag-La2Sn2O7/SnO2 Contacts

Preparation of Cubic Zinc Stannate Nanopowder and Its Application in Silver-Based Electrical Contact Material

Corrosion Resistance and Tribological Behavior of Ag-Ge/Nano-SiC Coatings Prepared by Pulse Electrodeposition

Wear and Corrosion Properties of 316L-SiC Composite Coating Deposited by Cold Spray on Magnesium Alloy

Influences of Tin Oxide Surface Modification on the Morphology and Performance of Sintered Ag/SnO2 Composite Powders

Comparison of the tribological properties of an ion sulfurized coating and a plasma sprayed FeS coating

Preparation and Arcing Characteristics of Ag/SnO2 Electrical Contacts

Electrochemical Properties and XPS Analysis of Ni-B/SiC Nanocomposite Coatings

Effects of Coating Process on the Characteristics of Ag–SnO2 Contact Materials

Microstructure and tribological properties of sulphide coating produced by ion sulphuration

Ni–SiC composite coatings with improved wear and corrosion resistance synthesized via ultrasonic electrodeposition

MICROSTRUCTURES AND WEAR-RESISTANCE BEHAV-IORS OF FERROUS SULFIDE COATINGS

The Influence of Sm Content on the Surface Morphology and Corrosion Behavior of Zn-Co-Sm Composite Coatings

Effect of pulse electroplating parameters on the morphology and corrosion resistance of Ag plating coating