Nanoscale Phase Engineering in Two-Dimensional Niobium Pentoxide Anodes toward Excellent Electrochemical Lithium Storage
Wanxing Zhang,Peixing Shen,Lizhi Qian,Yuan Wang,Hamidreza Arandiyan,Hitham Mahmoud,Xuemei Liu,Jun Wang,Xiaoliang Wang,Yanguo Liu,Hongyu Sun,Yanlong Yu
DOI: https://doi.org/10.1021/acsaem.1c00186
IF: 6.4
2021-04-19
ACS Applied Energy Materials
Abstract:Niobium pentoxide (Nb<sub>2</sub>O<sub>5</sub>) material is a promising anode for lithium-ion batteries (LIBs) due to the outstanding cycle performance and rate capability. However, the relatively low capacity severely limits the comprehensive performance. Generally, nanoscale engineering of the morphology and chemical composition of Nb<sub>2</sub>O<sub>5</sub> anodes is employed to improve electrochemical lithium storage. In this work, we promote the reservable capacity of a sheetlike Nb<sub>2</sub>O<sub>5</sub> anode by designing nanoscale phase interfaces between the nanodomains of T-Nb<sub>2</sub>O<sub>5</sub>, M-Nb<sub>2</sub>O<sub>5</sub>, and H-Nb<sub>2</sub>O<sub>5</sub> phases, which are generated by good control over the calcination of Nb<sub>3</sub>O<sub>7</sub>F precursor at high temperatures. Microstructural and chemical analyses show that the sample calcined at 750 °C (Nb<sub>2</sub>O<sub>5</sub>-750) has optimized structural advantages to efficiently store lithium ions. When evaluated as anodes for LIBs, the Nb<sub>2</sub>O<sub>5</sub>-750 sample shows excellent lithium storage properties. In specific, the Nb<sub>2</sub>O<sub>5</sub>-750 electrode delivers a reversible capacity of 270.4 mAh g<sup>–1</sup> at 1C after 200 cycles. At a high rate of 5C, the Nb<sub>2</sub>O<sub>5</sub>-750 electrode has a reversible capacity of 174 mAh g<sup>–1</sup> after 800 cycles. This work provides an alternative way to improve the ion storage in the electrodes with intrinsic polymorphic structures.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c00186?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c00186</a>.XRD patterns, additional SEM and TEM images, BET specific surface areas and pore size distributions, XPS spectra, CV profiles, charge–discharge curves of other Nb<sub>2</sub>O<sub>5</sub> samples, and EIS results (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00186/suppl_file/ae1c00186_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels