Abstract:A 12% Cr ferritic/martensitic steel, HT-9, has been used as a primary core material for nuclear reactors. The microstructure and mechanical properties of gas tungsten arc butt welded joints of HT-9 in as-welded, and as-tempered conditions have been explored. In as-welded condition, the fusion zone (FZ) contained a fresh martensite matrix with delta (δ)-ferrite. The δ-ferrite was rich in Cr and depleted in C compared with the matrix. The heat-affected zone (HAZ) could be divided into three areas as the distance from the fusion line increased: δ-ferrite/martensite duplex zone, fully recrystallized zone, and partly recrystallized zone. Prior austenitic grains did not coarsen in the δ-ferrite/martensite duplex zone due to the newly nucleated δ-ferrite grains and incompletely ferritizing (δ-ferrite) during the welding thermal cycle. The weldment microhardness distributed heterogeneously with values above 600 HV1.0 in the HAZ and FZ and 250 HV1.0 in the base metal (BM). Solute C in the matrix, induced by the dissolution of carbide during the welding process, dominated the microhardness variation. Low toughness was observed in the FZ with a quasi-cleavage fracture tested from − 80 to 20 °C. The tensile fracture occurred in the relatively soft BM tested from 20 to 600 °C. In as-tempered condition (760 °C for 1 h), M23C6-type carbides precipitated within the martensitic laths, the lath boundaries, and the δ-ferrite/martensite interfaces. Moreover, V, Cr, Mo-rich nitrides with very small size also precipitated in the δ-ferrite/martensite interface. The tempering treatment improved the homogenous distribution of weldment hardness significantly. Tensile fracture still occurred in the BM of the weldment specimens tested from 20 to 600 °C. The impact toughness improved significantly, but the ductile–brittle transaction temperature was − 12 °C which was higher than that of the normalized and tempered (N&T) BM. δ-ferrite was considered to be one of the major factors aggravating the impact toughness in the FZ.

Softening mechanism and failure behavior of 9Cr oxide dispersion strengthened steel resistance spot welded joint

Microstructure and Tensile Strength of the Bonded Interfaces and Parent Materials in W/ODS Steel Joints Fabricated by Direct SSDB

Synchrotron Study on Load Partitioning Between Ferrite/martensite and Nanoparticles of a 9cr ODS Steel

Microstructure of a Domestically Fabricated Dissimilar Metal Weld Joint (SA508-52M-309L-CF8A) in Nuclear Power Plant

Effect Mechanism of Softening Zone Constraint on Tensile Failure of High-Strength Steel Laser-Welded Joints

Effect of softening of 6082-T6 aluminum alloy CMT welded joints on mechanical properties and fracture behavior

The Role of HAZ Softening on Cross-Tension Mechanical Performance of Martensitic Advanced High Strength Steel Resistance Spot Welds

Failure behavior of resistance spot welded advanced high strength steel: The role of surface condition and initial microstructure

Microstructures and Ion-Irradiation Behaviour of Friction Stir Welded 12Cr-Ods Steel

Tensile shear fracture load bearing capability, softening of HAZ and microstructural characteristics of resistance spot welded DP-1000 steel joints

Study on Softening in HAZ and Its Influence on Welded Joints of X70 Pipeline Steel

A Study of Microstructure and Mechanical Properties for the Autogenous Single-Pass Butt Weldment of a Ferritic/Martensitic Steel Using Gas Tungsten Arc Welding

Study of Microstructure and Stress Corrosion Cracking Behavior in Welding Transition Zone of Ni-Based Alloys

Analysis of Strengthening Mechanisms in Nano-ODS Steel Depending on Preparation Route

Mechanical Behavior and Failure Mechanism of Q&P980 Steel During In Situ Post-Weld Heat Treatment (PWHT) Resistance Spot Welding

Microstructure and Mechanical Properties of the Welding Joint of A New Corrosion-Resisting Nickel-Based Alloy and 304 Austenitic Stainless Steel

Studies of the Characteristics and Size Effects of Softened Zone of Laser Welded 20mntib Joint

X-ray Microscopic and Thermodynamic Model Assessments of Softening in TIG-Welded AA 6061-T651

Insights into microstructure evolution and fracture mechanisms of welded joints of high strength steel patchwork components

Microstructural Characterization and Strengthening Mechanisms of a 12Cr-Ods Steel

Softening issue in the thick-plate friction pull plug welding of AA2219-T87