Abstract:For CO2 methanation reaction, a Mg species is often utilized as the alkaline promotor for Ni based catalysts to enhance the low-temperature catalytic activity. Herein, based on a pioneer ordered mesoporous NiO-Al2O3 catalyst, a Mg alkaline promotor had been incorporated into the ordered mesoporous framework via a one-pot evaporation induced self-assembly (EISA) strategy. As a result, the ordered mesoporous NiO-MgO-Al2O3 composite oxides with Mg/Al molar ratios in a wide range (0-10%) were successfully fabricated and directly utilized as the catalysts for CO2 methanation reaction. These mesoporous catalysts were carefully characterized by X-ray diffraction, N-2 adsorption-desorption, transmission electron microscopy, selected area electron diffraction, energy dispersive spectrometer, X-ray photoelectron spectroscopy, H-2 temperature-programmed reduction, and CO2 temperature-programmed desorption measurements. It was found that the ordered mesoporous materials with large specific surface areas (180.8-232.8 m(2) g(-1)), big pore volumes (0.37-0.43 cm(3) g(-1)), and narrow pore size distributions (around 9.5 nm) could be successfully retained after the calcination at 700 degrees C. The highly dispersed Ni species were strongly interacted with the mesoporous framework in the form of NiAl2O4 spinel. The incorporation of the Mg progressively increased the surface basicity of these catalysts, which could intensify the chemisorption and activation of CO2 during the CO2 methanation reaction. Therefore, the low-temperature catalytic activity was significantly enhanced. The "volcano-shape curve" relationship between the Mg/Al molar ratio and catalytic activity had been interestingly observed, suggesting only appropriate surface basicity could obtain the optimum catalytic activity. Besides, there was no evident deactivation over these mesoporous catalysts after 50 h long-term stability tests due to the confinement effect of the mesoporous framework. Therefore, the present ordered mesoporous NiO-MgO-Al2O3 materials could be considered as a series of potential catalyst candidates for CO2 methanation.

Co-Precipitated Ni-Mg-Al Hydrotalcite-Derived Catalyst Promoted with Vanadium for CO2 Methanation

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

An Active Manganese Promoted Ni/Al2O3 Catalyst for Low Temperature CO2 Methanation

Alkaline-promoted Ni based ordered mesoporous catalysts with enhanced low-temperature catalytic activity toward CO2 methanation

Optimizing CO2 methanation: effect of surface basicity and active phase reducibility on Ni-based catalysts

Enhancement of magnesium aluminate-based nickel and cobalt nanostructured catalysts with iron for improved performance in carbon dioxide methanation

Facile preparation of a Ni/MgAl2O4 catalyst with high surface area: enhancement in activity and stability for CO methanation

Cobalt-doped Ni-based catalysts for low-temperature CO 2 methanation

Methanation of CO2 and CO by (Ni,Mg,Al)-Hydrotalcite-Derived and Related Catalysts with Varied Magnesium and Aluminum Oxide Contents

CO 2 methanation reaction over La-modified NiAl catalysts derived from hydrotalcite-like precursors

An Al2O3-supported NiFe bimetallic catalyst derived from hydrotalcite precursors for efficient CO2 methanation

Development of Highly Stable Ni-Al 2 O 3 Catalysts for CO Methanation

Cobalt promoted Ni/MgAl2O4 catalyst in lean methane catalytic oxidation

Distinguished Roles with Various Vanadium Loadings of Cocr2-Xvxo4 (X=0-0.20) for Methane Combustion

Hierarchical hollow Ni/γ-Al2O3 catalyst derived from flower-like Ni-Al layered double hydroxide with stable catalytic performance for CO2 methanation

NiFe and CoFe nanocatalysts supported on highly dispersed alumina-silica: Structure, surface properties, and performance in CO2 methanation

Enhanced low-temperature catalytic performance in CO2 hydrogenation over Mn-promoted NiMgAl catalysts derived from quaternary hydrotalcite-like compounds

CO2 Methanation over CoNi Bimetal-Doped Ordered Mesoporous Al2O3 Catalysts with Enhanced Low-Temperature Activities

Insight and comprehensive study of Ni-based catalysts supported on various metal oxides for CO2 methanation

CO2 Methanation over Hydrotalcite-Derived Nickel/Ruthenium and Supported Ruthenium Catalysts

Ni-based Hydrotalcite-Derived Catalysts for Enhanced CO2 Methanation: Thermal Tuning of the Metal-Support Interaction