Abstract:For the traditional preparation method, it is challenging to fabricate a supported nickel catalyst with fine size at high loading. In this work, a group of La-modified mesostructured cellular foam (MCF)-derived nickel phyllosilicates was designed and synthetized by a hydrothermal method followed by an impregnation-modification of La2O3, whose Ni contents varied from 25.3 to 32.2 wt %. Both the special property of phyllosilicate and the addition of a La2O3 modifier played significant roles in achieving high Ni dispersion and excellent catalytic performance. The formed nickel phyllosilicate was beneficial to obtain small Ni nanoparticles (<5 nm) due to its strong metal-support interaction and high specific surface area; the addition of the La2O3 modifier could further reduce the Ni particle size and decrease the reduction difficulty of the fabricated samples. On the contrary, a large Ni particle size of 13.0 nm was observed on the impregnated Ni/MCF (N/M-Im) catalyst with a Ni content of 31.7 wt %. As a result, the nickel phyllosilicate catalyst showed higher catalytic activity than the impregnated one, and the La modifier could further improve the catalytic activity especially at low temperature (<400 °C). Among all catalysts, the modified phyllosilicate catalyst N/M-P-32-5L with 180 °C-32 h-hydrothermal treatment and La2O3 content of 5 wt % was the best owing to its small-sized Ni particles, high H2 and CO2 chemisorption capacity, large turnover frequency (TOF) value, and low activation energy of 69.83 kJ mol-1. In addition, the intermediates of formate and CO were detected through in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) analysis. In a 100 h-lifetime test under harsh conditions and 600 °C-steam treatment, N/M-P-32-5L showed both high sintering resistance of Ni particles and high thermal stability without the collapse of pores as well as decrease of catalytic activity, which was attributed to the special physical and chemical properties of MCF-derived nickel phyllosilicate, strong metal-support interaction over the catalyst, and the promotion of the La2O3 modifier.

CO 2 methanation reaction over La-modified NiAl catalysts derived from hydrotalcite-like precursors

Enhancement of CO2 Methanation over La-Modified Ni/SBA-15 Catalysts Prepared by Different Doping Methods

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Enhanced low-temperature CO2 methanation over La-promoted NiMgAl LDH derived catalyst: Fine-tuning La loading for an optimal performance

NiAlFe catalysts based on hydrotalcite-like precursors for low temperature CO 2 methanation: Electronic effects among components and intrinsic activity of Ni site

The Effect of La2O3 on Ni/Al2O3 Catalyst for Methanation at Very Low COx/H2 Ratio

Cobalt-doped Ni-based catalysts for low-temperature CO 2 methanation

Morphology Effect of La2O2CO3 on CO2 Methanation over Ni-Based Catalysts

Lanthanum-mediated enhancement of nickel nanoparticles for efficient CO 2 methanation

Development of Highly Stable Ni-Al 2 O 3 Catalysts for CO Methanation

Methanation of Carbon Dioxide over a Highly Dispersed Ni/La2O3 Catalyst

A highly active Ni catalyst supported on Mg-substituted LaAlO3 for carbon dioxide reforming of methane

Catalytic Methanation of CO2 over Ni Supported on Acidation Bentontie and Alkalization Bentontie

CO2 methanation over Ni/ZSM-5 catalysts: The effects of support morphology and La2O3 modification

Enhanced activity and stability of Ni/La2O2CO3 catalyst for CO2 methanation by metal-carbonate interaction

CO2 Methanation over CoNi Bimetal-Doped Ordered Mesoporous Al2O3 Catalysts with Enhanced Low-Temperature Activities

Enhanced low-temperature catalytic performance in CO2 hydrogenation over Mn-promoted NiMgAl catalysts derived from quaternary hydrotalcite-like compounds

CO<sub>2</sub> methanation over Ni/ZSM-5 catalysts: The effects of support morphology and La<sub>2</sub>O<sub>3</sub> modification

Lanthanum-Modified MCF-Derived Nickel Phyllosilicate Catalyst for Enhanced CO2 Methanation: A Comprehensive Study

Hierarchical hollow Ni/γ-Al2O3 catalyst derived from flower-like Ni-Al layered double hydroxide with stable catalytic performance for CO2 methanation

Highly Dispersed Ni-La Catalysts over Mesoporous Nanosponge MFI Zeolite for Low-Temperature CO2 Methanation: Synergistic Effect Between Mesoporous and Microporous Channels