Effects of the Separator MOF-Al 2 O 3 Coating on Battery Rate Performance and Solid–Electrolyte Interphase Formation

Lu-Ye Yang,Jian-Hua Cao,Wei-Hua Liang,Ya-Kun Wang,Da-Yong Wu

DOI: https://doi.org/10.1021/acsami.2c00390

2022-03-11

Abstract:Metal organic frameworks (MOFs) have unique advantages in optimizing the ionic conductivity of battery separators because of their rich cavity structure and highly ordered and connected pores. In this study, we used a hydrothermal method to synthesize a functional material, Ag-MOF crystal, as a separator coating content, and then studied the properties and application effect of the MOF-Al2O3-blended coating applying to a polyethylene (PE) separator (MOFxAl1–x/PE). Results show that MOF0.08Al0.92/PE (MOF/Al2O3 = 0.08:0.92) used in NCM811||Li cells significantly not only improves the fast charge–discharge performance of the cells but also inhibits the growth of lithium dendrites during long-term charge–discharge cycling; the Li+ transference number (tLi+) of the MOF0.08Al0.92/PE composite separator is 0.61; the Li||separator||Li half-cell circulates stably for 1000 h at varying current density from 0.5 to 10 mA cm–2 and only produces low overpotentials, indicating that MOF0.08Al0.92 stabilizes lithium. The initial capacity of the NCM811||Li cell using the MOF0.08Al0.92/PE separator is 165.0 mA h g–1, its capacity retention is 70.67% after 300 cycles at 5 C, and the interface resistance of the cells only increases from 13.8 to 31.5 Ω, whereas the capacity retention of Al2O3/PE separator batteries is only 40.41% (62.2 mA h g–1) under the same conditions. During the charge–discharge cycling, the MOF-Al2O3 coating induces the lithium anode to quickly form a stable and dense solid–electrolyte interphase layer, promotes the uniform deposition of Li+, and inhibits the growth of lithium dendrites as well.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.2c00390.Crystal data and structure refinement for Ag-MOF; XRD patterns of the Ag-MOF; SEM image of the MOF0.08Al0.92 coating layer; elemental mapping of Al, O, Ag, C, and N; TGA curves; DCS curves; stress–strain curves; Nyquist plots; LSV curves of PE, Al2O3/PE, MOF0.05Al0.95/PE, and MOF0.08Al0.92/PE separators; EDS mapping; charge and discharge profiles of MOF0.08Al0.92/PE separator cells at 0.2 C; electrochemical performance of Li||PE||Li and Li||MOF0.08Al0.92/PE||Li symmetrical cells; long-term cycle stability at 1.0 mA cm–2; and XPS of Li anodes recovered from galvanostatic Li plating/stripping of the Li|| Al2O3/PE||Li cell after 100 cycles at 1 mA cm–2 (PDF)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology