Balanced Charge Carrier Transport Mediated by Quantum Dot Film Post-organization for Light-Emitting Diode Applications
Yuljae Cho,Jongchul Lim,Meng Li,Sangyeon Pak,Zhao-Kui Wang,Ying-Guo Yang,Antonio Abate,Zhe Li,Henry J. Snaith,Bo Hou,SeungNam Cha
DOI: https://doi.org/10.1021/acsami.1c04821
2021-05-27
Abstract:In light-emitting diodes (LEDs), balanced electron and hole transport is of particular importance to achieve high rates of radiative recombination. Most quantum dot (QD)-based LEDs, however, employ infinitesimal core–shell QDs which inherently have different electron and hole mobilities. As QDs are the core building blocks of QD-LEDs, the inherent mobility difference in the core–shell QDs causes significantly unbalanced charge carrier transport, resulting in detrimental effects on performances of QD-LEDs. Herein, we introduce a post-chemical treatment to reconstruct the QD films through the solvent-mediated self-organization process. The treatment using various poly-alkyl alcohol groups enables QD ensembles to transform from disordered solid dispersion into an ordered superlattice and effectively modulate electron and hole mobilities, which leads to the balanced charge carrier transport. In particular, ethanol-treated QD films exhibit enhanced charge carrier lifetime and reduced hysteresis due to the balanced charge carrier transport, which is attributed to the preferential-facet-oriented QD post-organization. As a result, 63, 78, and 54% enhancements in the external quantum efficiency were observed in red, green, and blue QD-LEDs, respectively. These results are of fundamental importance to understand both solvent-mediated QD film reconstruction and the effect of balanced electron and hole transport in QD-LEDs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c04821?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c04821</a>.Absorption spectra of QD films, PL and time-resolved PL curves of QD films, parameters extracted by fitting time-resolved PL curves, SCLC curves, electron and hole mobilities, hysteresis curves, EL of QD-LEDs, FWHM characteristics, 3D AFM images of ZnO and QD film morphology, red, green, and blue QD-LED device characteristics, and CIE coordinates of red, green, and blue QD-LEDs (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c04821/suppl_file/am1c04821_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology