Abstract:In this paper, we discussed recent studies done in our laboratories with a floating catalyst chemical vapor deposition (CVD) method. We can grow single- or double-walled carbon nanotubes (SWNTs/DWNTs) with different kinds of catalysts. Single-walled carbon nanotubes without amorphous carbon coating were prepared by thermally decomposing acetylene (C2H2) at the temperature range of 750–1200°C with ferrocene as catalyst. While with sulfur promoted ferrocene catalyst, double-walled carbon nanotubes were mass-produced by pyrolizing C2H2 at the temperature range of 900–1100°C. Furthermore, tunable growth of DWNTs with different diameter was achieved in our experiment. It is found that DWNTs produced at lower carbon partial pressure have much smaller inner tubes, even DWNTs with the smallest inner diameter of 0.4nm was found in here. As convenient and effective tool, radial breathing mode (RBM) of Raman scattering technique can be used to distinguish SWNTs from DWNTs. In further studies of Raman scattering with DWNTs, the possible match of the inner tubes and the outer tubes according to the RBM bands was assigned, and different chirality types were discussed according to the diameter and chirality dependence of resonant Raman vibration. We also investigated the temperature-dependent frequency shift of resonant Raman spectra of DWNTs in the range of 78–650K. We found that different RBM peaks, which are relative to different tube diameters, have different temperature coefficient of frequency shift, and the larger diameter carbon nanotubes have more RBM frequency downshift with increasing temperature. It is ascribed to the RBM frequency variation to the temperature dependence of the stretching force constant of C–C bond. Besides, Polarized Raman spectra were preformed on well-aligned SWNTs structure fabricated through post-growth method and found that the angular dependence of Raman intensity is consistent well with the predictions of the resonance Raman theory.

A new application of synchrotron radiation to carbon nanotubes - shape control and purification

Efficiently producing single-walled carbon nanotube rings and investigation of their field emission properties

Microwave Purification of Large-Area Horizontally Aligned Arrays of Single-Walled Carbon Nanotubes

Shaping single walled nanotubes

Purification and characterization of single-walled carbon nanotubes produced by arc-discharge

Purification of Multi Walled Carbon Nanotubes (Mwcnts) Synthesized by Arc Discharge Set Up

Synthesis Of Large Quantity Single-Walled Carbon Nanotubes By Arc Discharge

A Treatment Method to Give Separated Multi-Walled Carbon Nanotubes with High Purity, High Crystallization and a Large Aspect Ratio

Purification of multi-walled carbon nanotubes and its surface modification

Purification of single-walled carbon nanotubes

Controllable preparation and properties of single-/double-walled carbon nanotubes

Structure modification of single-wall carbon nanotubes

Purification of Single-Wall Carbon Nanotubes

Effect of microwave irradiation on carbon nanotube fibers: exfoliation, structural change and strong light emission

Carbon nanotubes over novel catalysts

High Temperature Treatment and Characterization of Carbon Nanotubes

Purification and Preliminary Modification of Multi-walled Carbon Nanotubes

Efficient Purification Of Single-Walled Carbon Nanotube Fibers By Instantaneous Current Injection And Acid Washing

Irradiation Treatment of Multiwalled Carbon Nanotubes and Its Effect on the Thermal Properties of Their Composites with Epoxy Resin

Synthesis of Super-Long Carbon Nanotubes from Cellulosic Biomass under Microwave Radiation

Optimize the Properties of Carbon Nanotubes Synthesized using a Microwave Oven