Synthesis and Mechanism of High Structural Stability of Nickel-Rich Cathode Materials by Adjusting Li-Excess
Zhenlu Yu,Xingyu Qu,Tao Wan,Aichun Dou,Yu Zhou,Xiaoqi Peng,Mingru Su,Yunjian Liu,Dewei Chu
DOI: https://doi.org/10.1021/acsami.0c12541
2020-08-14
Abstract:It has been a long-term challenge to improve the phase stability of Ni-rich LiNi<i><sub>x</sub></i>Mn<i><sub>y</sub></i>Co<sub>1–<i>x</i>–<i>y</i></sub>O<sub>2</sub> (<i>x</i> ≥ 0.6) transition metal (TM) oxides for large-scale applications. Herein, a new structure engineering strategy is utilized to optimize the structural arrangement of Li<sub>1+<i>x</i></sub>(Ni<sub>0.88</sub>Mn<sub>0.06</sub>Co<sub>0.06</sub>)<sub>1–<i>x</i></sub>O<sub>2</sub> (NMC88) with a different Li-excess content. It was found that structure stability and particle sizes can be tuned with suitable Li-excess contents. NMC88 with an actual Li-excess of 2.7% (<i>x</i> = 0.027, Li/TM = 1.055) exhibits a high discharge capacity (209.1 mAh g<sup>–1</sup> at 3.0–4.3 V, 0.1 C) and maintains 91.7% after the 100th cycle at 1 C compared with the NMC88 sample free of Li-excess. It also performs a delayed voltage decay and a good rate capacity, delivering 145.8 mAh g<sup>–1</sup> at a high rate of 10 C. Multiscale characterization technologies including ex/in situ X-ray diffraction (XRD), focused ion beam (FIB) cutting-scanning electronic microscopy (SEM), and transmission electron microscopy (TEM) results show that a proper Li-excess (2.7%) content contributes to the formation of a broader Li slab, optimized cation mixing ratio, and even particle sizes. Therefore, NMC88 with a proper Li-excess is a good choice for next-generation cathode materials.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c12541?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c12541</a>.Detailed crystalline structural information of E00, E03, E06, E09, and E12 after refinement (Table S1); actual ratio of cations in different samples measured by ICP-AES (Table S2); detailed graphic Rietveld refinement results for E00, E03, E06, E09, and E12 (Figure S1); cyclic voltammetry profiles of E00, E03, E06, E09, and E12 (Figure S2); Nyquist plot of E00, E03, E06, E09, and E12 at a discharged state of 3.0 V upon cycling (Figure S3); detailed fitting resistance values of E00, E03, E06, E09, and E12 after different cycles at 1 C using the Zview program (Table S3); GITT profiles of E00, E03, E09, and E12 (Figure S4); and captured SEM pictures of FIB-prepared E03 and E09 after 100 cycles at 1 C (Figure S5) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c12541/suppl_file/am0c12541_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology