Abstract:Sodium alginate (SA) solution with high quality fraction was prepared by NaOH/urea, NaOH/thiourea/urea, NaOH/thiourea and LiOH/urea at low temperature. The results showed that we got 5.5 wt% SA solution by using 5.5 wt% LiOH/20 wt% urea. The viscosity of the solution was 62.44 Pa·s, which had declined by 64% compared to that of 5 wt% SA solution (176.12 Pa·s). The difference from the traditional low temperature dissolution principle is that the urea is mainly wrapped on the SA surface by the interaction between the OH- in LiOH through the ether bond (O) and the π bond in the SA instead of the -OH in the SA. Only the crystallization peak of urea appeared in the XRD spectrum. It indicated that urea was successfully wrapped on the surface of SA to form urea-LiOH-SA inclusion complex. The 23Na NMR showed that the interaction between Na+ and other ions or molecules around it increased at low temperature. Breaking strength of regenerated CA was 2.44 cN/dtex, which rose by about 21.39% compared to that of CA fiber (2.01 cN/dtex). The "groove" on the surface of regenerated fiber is denser and the section is more loosely compared with those of CA fiber.

Dissolution mechanism of sodium alginate and properties of its regenerated fiber under low temperature