Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Free standing membranes to study the optical properties of anodic TiO2 nanotube layers

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Temperature-dependent differences in wettability and photocatalysis of TiO 2 nanotube arrays thin films

Nanotube Film for Quantum Dots Sensitized Solar Cells

Synthesis and Photoelectrochemical Properties of Self-Organized Anodic TiO<sub>2</sub> Nanotube Arrays

Aligned metal oxide nanotube arrays: key-aspects of anodic TiO2 nanotube formation and properties

Free-standing open-ended TiO2 nanotube membranes and their promising through-hole applications

Fabrication and Photocatalytic Activity of Tio2 Nanofiber Membrane

Synthesis and Photoelectrochemical Properties of Self-Organized Anodic TiO2 Nanotube Arrays

Transparent TiO2 Nanotubes Arrays Directly Grown on Quartz Glass Used in Front- and Back-Side Irradiation Configuration for Photocatalytic H2 Generation

Biocompatible and freestanding anatase TiO2 nanomembrane with enhanced photocatalytic performance.

Photoelectrochemical performance of TiO2 photoanodes: Nanotube versus nanoflake electrodes

Comparative Analysis of Anodized TiO2 Nanotubes and Hydrothermally Synthesized TiO2 Nanotubes: Morphological, Structural, and Photoelectrochemical Properties

Surface Carbon Layer and Visible-Light Photocatalytic Activities of Carbon-Coated Tio (2) Nanotubes Synthesized in Organic Electrolytes

Photocurrent conversion efficiency of TiO2 nanotube photoanodes in dependence of illumination intensity

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

Different crystalline phases of aligned TiO2 nanotubes and their UV photoelectric properties

Synthesis And Photovoltaic Application Of High Aspect-Ratio Tio2 Nanotube Arrays By Anodization

Enhanced Performance of Dye-Sensitized Solar Cells based on TiO2 Nanotube Membranes using Optimized Annealing Profile

High-Temperature Annealing of TiO2 Nanotube Membranes for Efficient Dye-Sensitized Solar Cells

Crystal phase transition and properties of titanium oxide nanotube arrays prepared by anodization