Effect of Secondary Aging on Microstructure and Properties of Spray Formed Al-12.3Zn-2.2Mg-1.5Cu Alloy

Su, Ruiming

DOI: https://doi.org/10.1007/s11665-024-10266-3

IF: 2.3

2024-10-10

Journal of Materials Engineering and Performance

Abstract:The spray formed Al-12.3Zn-2.2Mg-1.5Cu alloy subjected to secondary aging of T6I4, underwent comprehensive investigation. Various tests including hardness measurement, friction and wear assessment, tensile testing, and electrochemical corrosion analysis were conducted. Additionally, scanning electron microscopy and transmission electron microscopy were utilized to examine the microstructural characteristics of the alloy. The experimental findings demonstrate that employing T6I4 significantly enhances the microstructure and morphology of the spray formed Al-12.3Zn-2.2Mg-1.5Cu alloy, leading to notable improvements in both its mechanical characteristics and resistance to corrosion. After subjecting the alloy to 8 h of single-stage aging at 120 °C subsequent to 35 h of secondary aging at 70 °C, fine and uniformly distributed η' and η phases were formed in the alloy. The mechanical properties of the alloy were improved with a hardness value of 211.2 HV, the friction and wear coefficient of 0.62, the wear amount of 8.2 mg, the tensile strength of 745 MPa, the yield strength of 715 MPa, and the elongation of 8%, respectively. The width of PFZ increased, and the GBPs showed a discontinuous distribution which alleviated the corrosion sensitivity. The self-corrosion current density and corrosion rate were 0.0318 mA cm −2 , 1.0393 mm a −1 .

materials science, multidisciplinary