Abstract:The present study reports a simple, template free and controllable one-step synthesis of a series of amorphous, crystalline, and triphasic TiO 2 nanoparticles utilizing titanium( IV ) ethoxide as a molecular precursor. By reacting the titanium ethoxide in a mixture of ethanol, acetic acid, and water at reflux temperatures while varying the ratios of the reaction components, it was possible to obtain TiO 2 nanoparticles possessing high surface areas and pore volumes as well as diverse crystalline structures. The synthesized nanoparticles were characterized by FT-IR, XRD, SEM, TEM, TG, DTA, DTG, DRS, and argon sorption. X-ray diffraction and sorption analyses conclusively show that using an excess of ethanol resulted in the formation of an amorphous TiO 2 with a high surface area. Furthermore, an increase in the water content while slightly reducing the amount of acid but keeping ethanol still at excess resulted in the formation of a crystalline anatase phase, whereas the reaction in the absence of ethanol led to the formation of a triphasic material consisting of anatase (40.5%), rutile (25.5%), and brookite (34%). Under the optimized conditions, it was possible to produce amorphous and crystalline porous titanium dioxide with high surface areas of 350 and 310 m 2 g −1 respectively at low temperatures without subsequent heat treatment, which is reflected in their catalytic properties. Investigation of the photocatalytic and catalytic abilities of the synthesized nanoparticles to degrade and to reduce methylene blue (MB), respectively, as well as reduction of nitroaromatic compounds in aqueous media revealed that the amorphous materials showed the best performance with degradation of up to 94–99% of MB within 10 minutes. The kinetic studies also revealed that all nanoparticles exhibited high catalytic activity for the reduction of MB within a short time (3–4 min) and showed good agreement with a pseudo-first-order reaction model. The derived rate constants for the catalytic reduction of 2-NP, 3-NP, 4-NP, 2-NA, and 3-NA (NP = nitrophenol and NA = nitroaniline) with amorphous TiO 2 nanoparticles ( Ti-9 ), as the best catalyst, are 0.67 min −1 , 0.24 min −1 , 1.46 min −1 , 0.56 min −1 , and 0.21 min −1 , respectively. From the data, we can deduce that a high specific surface area, the occurrence of defects as well as the crystallinity of the materials play an essential role in the photocatalytic and catalytic performance.

Epoxide-Assisted Synthesis of Photocatalytically Active TiO2 and Pt/TiO2 Aerogels

Novel modified nonalkoxide sol–gel synthesis of multiphase high surface area TiO2 aerogels for photocatalysis

Titania and Pt/titania aerogels as superior mesoporous structures for photocatalytic water splitting

Preparation and Heat Treatment of Titania Aerogels by Ambient Pressure Drying

Photocatalytic activity of epoxide sol–gel derived titania transformed into nanocrystalline aerogel powders by supercritical drying

One-Step Synthesis Of Bifunctional Tio2 Catalysts And Their Photocatalytic Activity

TiO2 Aerogel Composite High-Efficiency Photocatalysts for Environmental Treatment and Hydrogen Energy Production

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Synthesis of Rutile and Anatase TiO2 Nanoparticles from Ti-peroxy Compound Aqueous Solution with Polyols

Titania Nanoflowers with High Photocatalytic Activity

Octahedral Shaped PbTiO 3 -TiO 2 Nanocomposites for High-Efficiency Photocatalytic Hydrogen Production.

Pt/N–TiO2 Aerogel Composites Used for Hydrogen Production Via Photocatalysis Process

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Controllable and facile one-pot synthesis of high surface area amorphous, crystalline, and triphasic TiO2: catalytic and photocatalytic applications

Surface Energy-Driven Solution Epitaxial Growth of Anatase TiO2 Homostructures for Overall Water Splitting

A Highly Photoactive Nanocrystalline TiO_2 Aerogel Prepared by a Non-Alkoxide Sol-Gel Method

Preparation of monolithic titania aerogels with high surface area by a sol–gel process combined surface modification

One-pot microwave synthesis of Pd modified titanium dioxide nanocrystals for 3D aerogel monoliths with efficient visible-light photocatalytic activity in a heated gas flow reactor

Oxygen-vacancy-assisted construction of Ce–TiO2 aerogel for efficiently boosting photocatalytic CO2 reduction without any sacrifice agent

3D structured TiO 2 -based aerogel photocatalyst for the high-efficiency degradation of toluene gas

Synthesis of Bulk BaTiO 3 Aerogel and Characterization of Photocatalytic Properties