Abstract:The present study reports a simple, template free and controllable one-step synthesis of a series of amorphous, crystalline, and triphasic TiO 2 nanoparticles utilizing titanium( IV ) ethoxide as a molecular precursor. By reacting the titanium ethoxide in a mixture of ethanol, acetic acid, and water at reflux temperatures while varying the ratios of the reaction components, it was possible to obtain TiO 2 nanoparticles possessing high surface areas and pore volumes as well as diverse crystalline structures. The synthesized nanoparticles were characterized by FT-IR, XRD, SEM, TEM, TG, DTA, DTG, DRS, and argon sorption. X-ray diffraction and sorption analyses conclusively show that using an excess of ethanol resulted in the formation of an amorphous TiO 2 with a high surface area. Furthermore, an increase in the water content while slightly reducing the amount of acid but keeping ethanol still at excess resulted in the formation of a crystalline anatase phase, whereas the reaction in the absence of ethanol led to the formation of a triphasic material consisting of anatase (40.5%), rutile (25.5%), and brookite (34%). Under the optimized conditions, it was possible to produce amorphous and crystalline porous titanium dioxide with high surface areas of 350 and 310 m 2 g −1 respectively at low temperatures without subsequent heat treatment, which is reflected in their catalytic properties. Investigation of the photocatalytic and catalytic abilities of the synthesized nanoparticles to degrade and to reduce methylene blue (MB), respectively, as well as reduction of nitroaromatic compounds in aqueous media revealed that the amorphous materials showed the best performance with degradation of up to 94–99% of MB within 10 minutes. The kinetic studies also revealed that all nanoparticles exhibited high catalytic activity for the reduction of MB within a short time (3–4 min) and showed good agreement with a pseudo-first-order reaction model. The derived rate constants for the catalytic reduction of 2-NP, 3-NP, 4-NP, 2-NA, and 3-NA (NP = nitrophenol and NA = nitroaniline) with amorphous TiO 2 nanoparticles ( Ti-9 ), as the best catalyst, are 0.67 min −1 , 0.24 min −1 , 1.46 min −1 , 0.56 min −1 , and 0.21 min −1 , respectively. From the data, we can deduce that a high specific surface area, the occurrence of defects as well as the crystallinity of the materials play an essential role in the photocatalytic and catalytic performance.

Novel modified nonalkoxide sol–gel synthesis of multiphase high surface area TiO2 aerogels for photocatalysis

Epoxide-Assisted Synthesis of Photocatalytically Active TiO2 and Pt/TiO2 Aerogels

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Photocatalytic activity of epoxide sol–gel derived titania transformed into nanocrystalline aerogel powders by supercritical drying

Eco-Friendly Colloidal Aqueous Sol-Gel Process for TiO2 Synthesis: The Peptization Method to Obtain Crystalline and Photoactive Materials at Low Temperature

Preparation of monolithic titania aerogels with high surface area by a sol–gel process combined surface modification

TiO2 Aerogel Composite High-Efficiency Photocatalysts for Environmental Treatment and Hydrogen Energy Production

A Highly Photoactive Nanocrystalline TiO_2 Aerogel Prepared by a Non-Alkoxide Sol-Gel Method

Oxygen-vacancy-assisted construction of Ce–TiO2 aerogel for efficiently boosting photocatalytic CO2 reduction without any sacrifice agent

Titania and Pt/titania aerogels as superior mesoporous structures for photocatalytic water splitting

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Controllable and facile one-pot synthesis of high surface area amorphous, crystalline, and triphasic TiO2: catalytic and photocatalytic applications

TiO2 Nanoparticles with Adjustable Phase Composition Prepared by an Inverse Microemulsion Method: Physicochemical Characterization and Photocatalytic Properties

Synthesis of bulk BaTiO3 aerogel and characterization of photocatalytic properties

Regenerated cellulose as template for in-situ synthesis of monoclinic titanium dioxide nanocomposite carbon aerogel towards multiple application in water treatment

Easy-handling semi-floating TiO2-based aerogel for solar photocatalytic water depollution

Synthesis of Bulk BaTiO 3 Aerogel and Characterization of Photocatalytic Properties

Preparation of Monolithic Tio2 Aerogel Via Ambient Drying and Photocatalytic Degradation of Oily Wastewater

Structure and Photocatalytic Properties of Ni-, Co-, Cu-, and Fe-Doped TiO2 Aerogels

Modulating Charge Separation of Ce-TiO2 Aerogel Supported on Chitosan Derived Ordered Porous Carbonaceous Frameworks for Promoting CO2 Photoreduction Activity

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles