Abstract:Argon oxygen decarburization (AOD) refining as one type of secondary refining plays an important role in the steel industry. MgO–CaO and MgO–C bricks are widely used in AOD refining, and MgO–CaO bricks are easily hydrated. MgO–C bricks containing carbon easily pollute molten steel and have lower mechanical strength. In this study, ultra-low carbon MgO–C bricks containing C/MgAl2O4 composite powders used in AOD refining were explored. MgAlON as the strength phase was in situ generated in the composites (M3) containing 2 wt% C/MgAl2O4 composite powders. The samples were further compared with commercial MgO–CaO bricks (M1), which are currently used in the slag line of the AOD furnace, and the sample (M2) without the addition of C/MgAl2O4 composite powders. The hot modulus of rupture (HMOR) of M3 was the highest at 27.3 MPa, which increased 44% compared with that of M2 and increased 158% compared with that of M1. The number of thermal shock test cycles of M3 was 1.6 times that of M2. HMOR and cold crush strength (CCS) of samples after thermal shock resistance test were measured. The HMOR of M3 after 3 cycles of the thermal shock test was 2.1 times greater than that of M1. After 20 thermal shock cycles, the residual CCS ratio of M3 was highest, up to 94.6%. Improvement in the thermal shock resistance of the composites can be achieved by the addition of C/MgAl2O4 composite powders, which promote the generation of MgAlON. It was also found that the slag corrosion depth of M3 was the lowest at 64.7% of that of M2 and was 13% of that of M1. The internal micromorphologies researched by XRD and SEM and the corrosion mechanism revealed by thermodynamic calculations show that MgAlON was formed in situ after the corrosion test and endowed the composites with excellent properties.

Finegrained aluminium-chromium composite fireproof materials

Fabrication of Y2O3-doped MgO Refractory Raw Materials Based on Magnesium Hydroxide from Salt-Lake Brine

Enhanced corrosion resistance by simultaneous refinement of pore structures and phase composition: A novel lightweight microporous alumina-rich spinel (Mg0.4Al2.4O4)

Enhanced performance of low-carbon MgO–C refractories with nano-sized ZrO2–Al2O3 composite powder

A novel low thermal conductivity refractory aggregate for high-temperature applications: Lightweight microporous alumina-rich spinel (Mg0.4Al2.4O4)

Evaluation of aluminum dross as raw material for high-alumina refractory

The microstructure evolution and performance enhancement of MgO-C refractories by the addition of MA90 spinel micro-powder

Microstructure evolution, mechanical characteristics and erosion behavior of Cr2O3–Al2O3–MgO–ZrO2 refractories in molten reduction slag

Preparation and research of fine-grained alumina with high mechanical properties

Mechanism of in-situ formation of spinel and its effect on the mechanical properties of Al2O3–C refractories

Enhancement of thermal shock resistance of Al2O3–MgAl2O4 composites by controlling the content and distribution of spinel phase

Zirconium-strontium composite micro-alloyed high-toughness corrosion-resistant low-silicon-content aluminum-silicon-copper cast aluminum alloy and preparation method

Effect of raw material composition on microstructures and properties of microporous MgO–Mg(Al, Fe) 2 O 4 refractory aggregates

Influence of titania on sintering and thermal expansion property of periclase spinel unfired product

Assessing Magnesia Effect on Preparing Refractory Materials from Ferrochromium Slag

Microstructures and strength of microporous MgO-Mg(Al, Fe)2O4 refractory aggregates

Mechanical properties and microstructure evolution of MgO–Al–C slide plate refractories in presence of Al powder-modified magnesia aggregates

Significant improvement of slag corrosion resistance and thermal shock resistance of corundum‐based dry vibratable refractory by addition of Fe–Si 3 N 4

Enhanced performance of ultra-low carbon MgO–C bricks by the addition of special C/MgAl2O4 composite powders

Development of Magnesium Aluminate (MgAl2O4) Nanoparticles for refractory crucible application

Microstructure and mechanical properties of CaAl12O19 reinforced Al2O3-Cr2O3 composites