Abstract:The in-situ synthesized mullite bonded SiC ceramics for solar thermal tower plant were prepared from Silicon carbide (SiC), manufactured aluminum hydroxide (Al(OH)3) and Suzhou kaolin via semi-dry pressing and pressureless firing. The results indicate that sample B3 (designed mullite content 15 wt%) fired at 1 400 °C exhibited optimal performance with a bending strength of 97.41 MPa. Sample B3 can withstand 30-cycles thermal shock without cracking (wind cooling from 1 100 °C to room temperature), and the bending strength after thermal shock decreased by 17.92%. When the service temperature is 600 °C, the thermal diffusivity, specific heat capacity, thermal conductivity and heat capacity are 6.48×10−2 cm2·s−1, 0.69 kJ·kg−1· K−1, 9.62 W·m−1·K−1 and 977.76 kJ·kg−1, respectively. The XRD and SEM results show that SiC, mullite, α-quartz, and tridymite are connected closely, which gives the material a good bending strength. After 30-time thermal shock cycles, the structure of samples becomes loose. SiC grains are intersectingly arranged with rodshape mullite, exhibiting a favorable thermal shock resistance. The addition of Al(OH)3 and Suzhou kaolin can accelerate the synthesis of mullite, thus to reduce the firing temperature effectively. The volume effect of tridymite is relatively small, improving the thermal shock resistance of materials. A higher designed mullite content yields a lower loss rate of bending strength. The mullite content should not be more than 15 wt% or else the bending strength would be diminished.

Low‐temperature and pressureless in‐situ self‐assembled SiC w / SiC composite ceramics for solar thermal absorber and storage integration

Scalable All-Ceramic Nanofilms As Highly Efficient and Thermally Stable Selective Solar Absorbers

Bamboo derived SiC ceramics-phase change composites for efficient, rapid, and compact solar thermal energy storage

Eco-friendly and large porosity wood-derived SiC ceramics for rapid solar thermal energy storage

Loofah-derived eco-friendly SiC ceramics for high-performance sunlight capture, thermal transport, and energy storage

Fabrication of SiCN(O) Aerogel Composites with Low Thermal Conductivity by Wrapping Mesoporous Aerogel Structures over Mullite Fibers

Preparation and characterization of mullite-silicon carbide heat absorbing ceramics for solar thermal tower plant

Enhanced thermochemical energy storage properties of SiC-doped calcium-based material with steam addition during heat charging process

Fabrication, Microstructure, and Properties of SiC/Al 4 SiC 4 Multiphase Ceramics Via an In-Situ Formed Liquid Phase Sintering

Fabricating superior thermal conductivity SiC–AlN composites from photovoltaic silicon waste

Tailoring the thermophysical properties of porous SiC framework reinforced Al-Mg-Si composites by Si alloying content for thermal energy management

The Thermal, Electrical and Mechanical Properties of Porous Α-Sic Ceramics Bonded with Ti3SiC2 and Β-Sic Via Low Temperature In-Situ Reaction Sintering

Fabrication, microstructure, and properties of SiC/Al4SiC4 multiphase ceramics via an in-situ formed liquid phase sintering

Low-temperature synthesis of dense Si-based nitride ceramics for solar thermal storage: Role of cordierite as sintering additive

Super Thermal Insulation SiC Aerogel with High Elasticity and Good Adsorption Performance Prepared by Constructing Coaxial Precursor

Preparation and characterization of lightweight SiC frameworks by connecting SiC fibers with SiC joints

AlN micro-honeycomb reinforced stearic acid-based phase-change composites with high thermal conductivity for solar-thermal-electric conversion

Foam-gelcasting preparation of porous SiC ceramic for high-temperature thermal insulation and infrared stealth

Thermal shock resistance and oxidation resistance of MgAl2O4–Si3N4 ceramics for solar thermal absorber: The effects of TiO2 additive content

In-situ synthesis and microstructural evolution of a SiC reinforced Al-50Si composite exhibiting exceptional thermal properties

Preparation, mechanical, dielectric and microwave absorption properties of hierarchical porous SiCnw-Si3N4 composite ceramics