Abstract:This work investigates the catalytic performance of nanocomposite Ni/ZrO2-AN catalyst consisting of comparably sized Ni (10–15nm) and ZrO2 (15–25nm) particles for hydrogen production from the cyclic stepwise methane reforming reaction with either steam (H2O) or CO2 at 500–650°C, in comparison with a conventional Ni/ZrO2-CP catalyst featuring Ni particles supported by large and widely sized ZrO2 particles (20–400nm). Though both catalysts exhibited similar activity and stability during the reactions at 500 and 550°C, they showed remarkably different catalytic stabilities at higher temperatures. The Ni/ZrO2-CP catalyst featured a significant deactivation even during the methane decomposition step in the first cycle of the reactions at ≥600°C, but the Ni/ZrO2-AN catalyst showed a very stable activity during at least 17 consecutive cycles in the cyclic reaction with steam. Changes in the catalyst beds at varying stages of the reactions were characterized with TEM, XRD and TPO–DTG and were correlated with the amount and nature of the carbon deposits. The Ni particles in Ni/ZrO2-AN became stabilized at the sizes of around 20nm but those in Ni/ZrO2-CP kept on growing in the methane decomposition steps of the cyclic reaction. The small and narrowly sized Ni particles in the nanocomposite Ni/ZrO2-AN catalyst led to a selective formation of filamentous carbons whereas the larger Ni particles in the Ni/ZrO2-CP catalyst a preferred formation of graphitic encapsulating carbons. The filamentous carbons were favorably volatilized in the steam treatment step but the CO2 treatment selectively volatilized the encapsulating carbons. These results identify that the nature but not the amount of carbon deposits is the key to the stability of Ni/ZrO2 catalyst and that the nanocomposite Ni/ZrO2-AN would be a promising catalyst for hydrogen production via cyclic stepwise methane reforming reactions.

Highly-stable Ni–Zn catalyst on USY zeolite support for low temperature methane pyrolysis

High Temperature Methanation over Ni Catalysts Supported on High Surface Area ZnxMg1-xAl2O4: Influence on Zn Loading

High-Stability ZnAl2O4 Spinel-Supported Nickel Catalyst for High-Temperature Syngas Methanation

Investigating the Effect of Ni Loading on the Performance of Yttria-Stabilised Zirconia Supported Ni Catalyst during CO2 Methanation

Tuning metal-support interactions in nickel-zeolite catalysts leads to enhanced stability during dry reforming of methane

Nanocomposite Ni/ZrO 2: Highly active and stable catalyst for H 2 production via cyclic stepwise methane reforming reactions

Insights on the Highly Stable and Coke-Resistant Nickel/Zirconia Nanocatalyst for the Methanation of Carbon Dioxide

Synthesis of nickel catalysts supported on Zr-doped ordered mesoporous Al2O3 and their catalytic performance for low-temperature CO2 reforming of CH4

Partial Oxidation Of Methane To Syngas Over Ni-Based Catalysts

Overcoming the kinetic and deactivation limitations of Ni catalyst by alloying it with Zn for the dry reforming of methane

Highly Active and Stable Ni/ZrO2 Catalyst for Syngas Production by CO2 Reforming of Methane

Insights into the Zn Promoter for Improvement of Ni/SiO 2 Catalysts Prepared by the Ammonia Evaporation Method toward CO 2 Methanation

Impact of varied zeolite materials on nickel catalysts in CO 2 methanation

Catalytic Methanation of Syngas over Ni-based Catalysts with Different Supports

Response Surface Methodology for Ni-Zeolite Catalyst Optimization in Syngas Production

Carbon Dioxide Reforming of Methane over Nickel-Supported Zeolites: A Screening Study

Mn and Mg Dual Promoters Modified Ni/α-Al2O3 Catalysts for High Temperature Syngas Methanation

Efficient and Stable Ni/ZSM-5@MCM-41 Catalyst for CO 2 Methanation

Enhanced Catalytic Performance of PtSn Catalysts for Propane Dehydrogenation by a Zn-modified Mg(Al)O Support

Stable Ni/ZrO2 catalyst for carbon dioxide reforming of methane

Catalytic performance of Ni catalysts for steam reforming of methane at high space velocity