Abstract:We have constructed heterojunction iodide ligand PbS quantum dot (QD) and ZnO nanowire (NW) solar cells. In these interdigitated structures, PbS QDs are well-embedded within ZnO NWs grown on a dense ZnO layer. A Au back contact is directly formed on the iodide ligand PbS QD surface layer. In the widely studied colloidal QD-based heterojunction solar cells, the PbS QD active layer is sandwiched between the hole-blocking layer (or electron-accepting layer) and the electron-blocking layer (EBL) (or hole-transport layer). In contrast, our solar cells contain no EBL except an additional thin PbS QD capping layer, which was deposited on the interdigitated layer to ensure the complete infiltration of the PbS QDs, and prevent shortening between the ZnO NWs and Au back contact. The interdigitated layer was constructed using a layer-by-layer dip-coating method to achieve sufficient infiltration of PbS QDs in the ZnO NWs. Owing to highly efficient charge separation in the interdigitated structure, our cell achieved a high external quantum efficiency in the visible and infrared regions, despite using only iodide ligand PbS QDs. Using cross-sectional Kelvin probe force microscopy, we confirmed that the PbS QD capping layer formed between the ZnO NW and Au back contact intrinsically functioned as an EBL. Consequently, the solar cells with ZnO NWs and iodide ligand PbS QDs maintained their performance after 500 days of storage in air without encapsulation. This stability performance surpasses most of the previously reported solar cells with PbS QDs. An encapsulated 1.0 cm2 solar cell maintained its power output for over 75 h under continuous one-sun illumination with no significant degradation. The proposed solar cell architecture with an automatically embedded EBL can realize highly efficient and stable colloidal QD-based solar cells. Moreover, the interdigitated architecture concept can be extended to various organic and inorganic hybrid solar cells.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c00723?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c00723</a>.Chemicals and reagents, synthesis of PbS CQDs, synthesis of ZnO NWs, list of previous works on the NW-PbS quantum dot solar cells, best solar cell performance parameters of <a class="internalNav" href="#fig1">Figure </a><a class="internalNav" href="#fig1">1</a>, AFM images of the ZnO NW/PbS QD interdigitated layer and those with different capping layers, performance parameters of solar cells with the optimal EDT-EBL thickness and ZnO NW length, KFM measurement conditions, temperature dependence of I–V characteristics of the solar cells, and solar cell characteristics measured in the course of the air stability test (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00723/suppl_file/ae1c00723_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Low-Temperature-Processed ZnO Electron Transport Layers for PbS Colloidal Quantum Dot-Based Solar Cells

Low-temperature Preparation Achieving 10.95%-Efficiency of Hole-Free and Carbon-Based All-Inorganic CsPbI3 Perovskite Solar Cells

ZnO/SrTiO3, ZnO/WO3, and ZnO/Zn2SnO4 Bilayer as Electron Transport Layers for Lead Sulfide Colloidal Quantum Dots Solar Cells

A low-temperature solution-processed indium incorporated zinc oxide electron transport layer for high-efficiency lead sulfide colloidal quantum dot solar cells

Organic Ligand‐Free ZnO Quantum Dots for Efficient and Stable Perovskite Solar Cells

Low-temperature aqueous solution processed ZnO as an electron transporting layer for efficient perovskite solar cells

Solution Annealing Induces Surface Chemical Reconstruction for High-Efficiency PbS Quantum Dot Solar Cells

Efficient PbSe Colloidal Quantum Dot Solar Cells Using SnO2 as a Buffer Layer

ZnO/ZnS Core-Shell Composites for Low-Temperature-processed Perovskite Solar Cells

Highly Stable Interdigitated PbS Quantum Dot and ZnO Nanowire Solar Cells with an Automatically Embedded Electron-Blocking Layer

Efficient inverted polymer solar cells using low-temperature zinc oxide interlayer processed from aqueous solution

Aqueous Solution Processed, Ultrathin ZnO Film with Low Conversion Temperature As the Electron Transport Layer in the Inverted Polymer Solar Cells

Low‐Temperature Solution‐Processed ZnO Electron Transport Layer for Highly Efficient and Stable Planar Perovskite Solar Cells with Efficiency over 20%

Low-Temperature Synthesis of FeOOH Quantum Dots As Promising Electron-Transporting Layers for High-Performance Planar Perovskite Solar Cells

Efficient PbS Quantum Dot Solar Cells with Both Mg-Doped ZnO Window Layer and ZnO Nanocrystal Interface Passivation Layer.

Cation‐Exchange Synthesis of Highly Monodisperse PbS Quantum Dots from ZnS Nanorods for Efficient Infrared Solar Cells

Annealing-Temperature Dependent Carrier-Transportation in ZnO/PbS Quantum Dot Solar Cells Fabricated Using Liquid-Phase Ligand Exchange Methods

Low‐Temperature Synthesis of SnO2 Nanocrystals As Electron Transport Layers for High‐Efficiency CsPbI2Br Perovskite Solar Cells

Zinc Oxide Coated Carbon Dot Nanoparticles as Electron Transport Layer for Inverted Polymer Solar Cells

Low-Cost, Air-Processed Quantum Dot Solar Cells via Diffusion-Controlled Synthesis

Enhanced Electron Transportation by Dye Doping in Very Low-Temperature (< 130 Degrees C)-Processed Sol-Gel ZnO Toward Flexible Organic Solar Cells