Abstract:Background: Fe80B20 amorphous alloys exhibit excellent soft magnetic properties, high abrasive resistance and outstanding corrosion resistance. In this work, Fe80B20 amorphous micro-fibers with HC of 3.33 Oe were firstly fabricated and the effects of annealing temperature on the structure and magnetic properties of the fibers were investigated. Methods: In this study, Fe80B20 amorphous fibers were prepared by the single roller melt-spinning method. The structures of as-spun and annealed fibers were investigated by X-ray diffractometer (XRD) (PANalytical X,Pert Power) using Cu Kα radiation. The morphology of the fibers was observed by scanning electron microscopy (SEM) (HITACHI-S4800). Differential scanning calorimetry (DSC) measurements of the fibers were performed on Mettler Toledo TGA/DSC1 device under N2 protection. Vibrating sample magnetometer (VSM, Versalab) was used to examine the magnetic properties of the fibers. The resonance behavior of the fibers was characterized by an impedance analyzer (Agilent 4294A) with a home-made copper coil. Results: The X-ray diffusion (XRD) patterns show that the fibers remain amorphous structure until the annealing temperature reaches 500°C. The differential scanning calorimetry (DSC) results show that the crystallization temperature of the fibers is 449°C. The crystallization activation energy is calculated to be 221 kJ/mol using Kissinger formula. The scanning electron microscopy (SEM) images show that a few dendrites appear at the fiber surface after annealing. The result indicates that the coercivity HC (//) and HC (⊥) slightly increases with increasing annealing temperature until 400°C, and then dramatically increases with further increasing annealing temperature which is due to significant increase in magneto-crystalline anisotropy and magneto-elastic anisotropy. The Q value firstly increases slightly when the annealing temperature rises from room temperature (RT) to 300°C, then decreases until 400°C. Eventually, the value of Q increases to ~2000 at annealing temperature of 500°C. Conclusions: In this study, Fe80B20 amorphous fibers with the diameter of 60 μm were prepared by the single roller melt-spinning method and annealed at 200°C, 300°C, 400°C, and 500°C, respectively. XRD results indicate that the fiber structure remains amorphous when the annealing temperature is below 400°C. α-Fe phase and Fe3B phase appear when the annealing temperature rises to 500°C, which is above the crystallization temperature of 449°C. The recrystallization activation energy is calculated to be 221 kJ/mol. The coercivity increases with increasing annealing temperature, which attributes to the increase of total anisotropy. All the as-spun and annealed fibers exhibit good resonance behavior for magnetostrictive sensors.

Properties optimization analysis of amorphous ribbons in acoustic magnetic labels

Effect of heat treatment on the properties of amorphous ribbons in acoustic magnetic tags

Effect of Annealing Temperature on Permeability and Giant Magneto-Impedance of Fe-based Amorphous Ribbon

Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

Magnetic and Mechanical Properties of the Amorphous Alloys

Crystallization kinetics and magnetic properties of Fe 63.5Co10Si13.5B9Cu 1Nb3 nanocrystalline powder cores

Revealing the effects of cooling rate on soft magnetic properties of (Fe0·9Co0·1)86Ni1B13 amorphous alloy

Crystallization Kinetics and Magnetic Properties of Fe73.5si13.5b9cu1nb1v2 Nanocrystalline Powder Cores

Effect of magnetic field annealing on the soft magnetic properties of CoFeSiB ribbon and its fluxgate performance

Magnetoinductance Effect in Co 67 Fe 4 Si 14.5 B 14.5 Amorphous Ribbons Annealed with Different Orientation Magnetic Fields

Influence of Magneto-Thermal Treatments on Longitudinally Driven Giant Magneto-Impedance Effect in Co-Fe-Si-B Amorphous Ribbons

Improving the degradation and magnetization performance of FePC amorphous alloys by annealing treatment

Influence of Annealing Process on Soft Magnetic Properties of Fe-B-C-Si-P Amorphous Alloys

Influence of Annealing on the Magnetic Entropy Changes in Fe81.6Mo4Zr3.3Nb3.3B6.8Cu1 Amorphous Ribbons

Effects of annealing on the structure and magnetic properties of Fe80B20 magnetostrictive fibers

Effect of CO gas on surface profile and magnetic properties of Fe–Si–B amorphous ribbons

Effects of Microwave-Assisted Annealing on the Structure and Magnetic Properties of (nd0.75pr0.25)9fe72ti1zr3mn X Mo4−x B10.5C0.5 Amorphous Ribbons

Differences in the Structure and Magnetic Properties of (nd0.75pr0.25)(9.5)fe76x4b10.5 (x=nb, Zr) Ribbons by Conventional and Microwave-Assisted Annealing Treatment

Effect of transverse magnetic field annealing on the magnetic properties and microstructure of FeSiBNbCuP nanocrystalline alloys

Crystallization Process of Nanocrystalline (FeCo)(78)Nb6B15Cu1 Alloy and Its Magnetic Characterization

Study of dielectric and magnetic properties with Fe76Si19.4Nb2.7Cu1.7P0.2 ribbons