Synthesis and characterization of mesoporous sodalite and investigation of the effects of inorganic salts on its structure and properties

Longjie Cui,Ruyue Han,Lu Yang,Yibo Wu,Rujing Pei,Fuxiang Li

DOI: https://doi.org/10.1016/j.micromeso.2020.110385

IF: 5.876

2020-10-01

Microporous and Mesoporous Materials

Abstract:<p>Mesoporous sodalite was prepared using a bridged polysilsesquioxane monomer as the mesoporogen in the presence of chloride-containing salts (NaCl, KCl, and NH₄Cl), and characterized using different analytical techniques. As the amount of organosiloxane increased in the synthetic mixture, the total BET surface areas of samples initially increased and then decreased. When 6 ml mesoporogen was added, the prepared sodalite sample showed the largest external BET surface area of 179 m²/g. Meanwhile, the addition of salts promoted crystallization, and the sodalite surface area reached 295 m²/g, making its skeletal framework more regular and weakening the template effect. Furthermore, mesoporous sodalite samples were used to evaluate the alkali catalytic performance of 1,3-dichloropropanol during the preparation of epichlorohydrin. The results showed that a larger surface area and pore volume were beneficial to the conversion and selectivity of this reaction.</p>

materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied

What problem does this paper attempt to address?

This paper aims to solve the following main problems:

1. **Synthesis of Mesoporous Sodalite (MSOD)**: By using Bridged Polysilsesquioxane Monomer (BPM) as a mesopore - generating agent, sodalite with a mesoporous structure was successfully synthesized. The effects of different amounts of BPM on the specific surface area and pore volume of the synthesized samples were studied.

2. **Effects of inorganic salts on the structure and properties of sodalite**: The roles of inorganic salts such as sodium chloride (NaCl), potassium chloride (KCl) and ammonium chloride (NH₄Cl) in the synthesis process were explored. It was found that these inorganic salts can promote the crystallization of sodalite, improve the regularity of its framework structure, weaken the template effect and reduce the formation of inter - crystalline amorphous substances.

3. **Catalytic performance evaluation**: The alkali - catalytic performance of the synthesized mesoporous sodalite samples in the reaction of preparing epichlorohydrin (ECH) from 1,3 - dichloropropanol (1,3 - DCH) was evaluated. It was found that a larger specific surface area and pore volume are helpful to improve the conversion rate and selectivity of the reaction.

### Specific problem analysis

- **Synthesis of mesoporous sodalite**:
- Mesoporous sodalite was prepared by a hydrothermal synthesis method using BPM as a mesopore - generating agent.
- The effects of different amounts of BPM on the specific surface area and pore volume of the samples were studied. The results showed that as the amount of BPM increased, the specific surface area of the sample first increased and then decreased, and when the amount of BPM was 6 mL, the specific surface area of the sample reached a maximum value of 179 m²/g.

- **Effects of inorganic salts**:
- The addition of inorganic salts (NaCl, KCl, NH₄Cl) can significantly improve the crystallinity of sodalite and make its framework structure more regular.
- The addition of inorganic salts also increased the specific surface area and pore volume of the samples. Among them, NH₄Cl had the most obvious effect, and the specific surface area of the sample reached 295 m²/g and the pore volume reached 0.4 cm³/g.

- **Catalytic performance**:
- The mesoporous sodalite samples showed excellent catalytic performance in the reaction of preparing epichlorohydrin from 1,3 - dichloropropanol.
- A larger specific surface area and pore volume are helpful to improve the conversion rate and selectivity of the reaction, especially at lower temperatures.
- Among them, the MSOD - NaCl sample had the best catalytic performance at high temperatures, which was related to its higher crystallinity and specific surface area.

In conclusion, this paper shows the potential application value of mesoporous sodalite in catalytic reactions by synthesizing mesoporous sodalite and studying the effects of inorganic salts on its structure and properties.