Abstract:Hierarchical meso-macroporous materials have attracted much attention due to their potential applications in catalysis, sorption, and separation. The incorporation of interconnected macropores in mesoporous materials is very useful because macropores can favor mass transfer and reduce transport limitations. However, it still remains a challenge to fabricate ordered mesoporous channels in the bicontinuous macroporous framework walls. This paper reports a double-templating route based on a sol-gel method to prepare hierarchical meso-macroporous silica monoliths. The obtained material shows a bicontinuous macroporous structure with highly ordered meso-channels distributing inside the macroporous skeleton walls. The bimodal pore structure was formed Under the action of the two templates. The organic polymer was added to induce a phase separation taking place at the sol-gel transition and thus form the bicontinuous macroporous structure. Meanwhile, a nonionic surfactant was introduced to template the formation of ordered mesostructure inside the macroporous skeleton walls. As characterization by scanning electron microscopy, transmittance electron microscopy, N-2,, physisorption, and X-ray diffraction, the resulting silica monolith exhibits Specific Surface area as high as 880 m(2)/g and pore volume as large as 1.2 cm(3)/g. The hexagonally ordered mesopores are highly centered at 5.8 nm. Besides, through optimizing the synthesis procedure, the monolith morphology of the resulting materials can be perfectly preserved during the wet gel drying process, and thus a crack-free hierarchical silica monolith with centimeter scale can be obtained.

PREPARATION OF MACRO-MESOPORE SiO2 MICROSPHERES WITH A MIXED TEMPLATE UNDER ASSOCIATION ACTION OF K2SO4

Fabrication of Porous Silica Microspheres under the Assistance of Solid Template

Monodisperse molecular sieve microsphere and preparation method thereof

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

Synthesis of mesoporous silica using block copolymer-cationic surfactant mixtures as templates

Influence of preparation method on the morphology of voided SiO2 microspheres prepared by template process

Triblock Copolymer and Poly(Ethylene Glycol) As Templates for Monolithic Silica Material with Bimodal Pore Structure

Morphology controlling of micrometer-sized mesoporous silica spheres assisted by polymers of polyethylene glycol and methyl cellulose

Silicon dioxide hollow microspheres with porous composite structure: Synthesis and characterization

Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents

Preparation of silica microspheres with bimodal pore structure in micro-channel

Double-Templating Synthesis of Hierarchical Meso-Macroporous Silica Monolith

Synthesis and characterization of mesoporous sodalite and investigation of the effects of inorganic salts on its structure and properties

Preparation of Micrometer-Sized Mesoporous Silica Spheres Assisted by Methyl Cellulose

A Systematic Investigation Of The Formation Of Ordered Mesoporous Silicas Using Poly(Ethylene Oxide)-B-Poly(Methyl Methacrylate) As The Template

Construction and Preparation Mechanism of Hierarchically Porous Sio2 Monoliths

Synthesis of Mesoporous Silica Using Triton X - 100 As Template and Study of the Morphology

Core-template-free Synthesis of Molecularly Ethane-Bridged Hollow Mesoporous Silica Spheres from Acid-Hydrolyzed Precursor

Synthesis of Silicate Materials with Micro/Macroporous Bimodal Pore Systems

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates

Synthesis of Colloidal Mesoporous Silica Spheres with Large Through-Holes on the Shell