Abstract:Giant dielectric (GD) oxides exhibiting extremely large dielectric permittivities (ε' > 104) have been extensively studied because of their potential for use in passive electronic devices. However, the unacceptable loss tangents (tanδ) and temperature instability with respect to ε' continue to be a significant hindrance to their development. In this study, a novel GD oxide, exhibiting an extremely large ε' value of approximately 7.55 × 104 and an extremely low tanδ value of approximately 0.007 at 103 Hz, has been reported. These remarkable properties were attributed to the synthesis of a Lu3+/Nb5+ co-doped TiO2 (LuNTO) ceramic containing an appropriate co-dopant concentration. Furthermore, the variation in the ε' values between the temperatures of -60 °C and 210 °C did not exceed ±15% of the reference value obtained at 25 °C. The effects of the grains, grain boundaries, and second phase particles on the dielectric properties were evaluated to determine the dielectric properties exhibited by LuNTO ceramics. A highly dense microstructure was obtained in the as-sintered ceramics. The existence of a LuNbTiO6 microwave-dielectric phase was confirmed when the co-dopant concentration was increased to 1%, thereby affecting the dielectric behavior of the LuNTO ceramics. The excellent dielectric properties exhibited by the LuNTO ceramics were attributed to their inhomogeneous microstructure. The microstructure was composed of semiconducting grains, consisting of Ti3+ ions formed by Nb5+ dopant ions, alongside ultra-high-resistance grain boundaries. The effects of the semiconducting grains, insulating grain boundaries (GBs), and secondary microwave phase particles on the dielectric relaxations are explained based on their interfacial polarizations. The results suggest that a significant enhancement of the GB properties is the key toward improvement of the GD properties, while the presence of second phase particles may not always be effective.

A new acceptor-donor co-doping TiO 2 -based ceramics with superior dielectric property and insulation performance

Enhanced dielectric properties and improved thermal stability in TiO 2 -based ceramics by Cu and Nb co-doping

Novel SrTiO 3 -based ceramics with colossal permittivity, low dielectric loss, and high insulation resistivity via defect engineering

Colossal Permittivity and Ultralow Dielectric Loss in Nb-doped SrTiO 3 Ceramics

Thermal stable and ultralow dielectric loss in (Gd0.5Ta0.5) Ti1-O2 giant permittivity ceramics by defect engineering

Bismuth Oxide Modified Europium and Niobium Co-Doped Titanium Dioxide Ceramics: Colossal Permittivity and Low Dielectric Loss Design

Colossal Dielectric Performance of Pure Barium Titanate Ceramics Consolidated by Spark Plasma Sintering

Grain-boundary engineering inducing thermal stability, low dielectric loss and high energy storage in Ta+Ho co-doped TiO2 ceramics

Enhanced dielectric performance of Niobium and Thulium modified rutile TiO 2 ceramics by defect regulation

Ag+/W6+ Co-Doped Tio2 Ceramic With Colossal Permittivity And Low Loss

Defect chemistry and optimized dielectric properties of Ni1-δO ceramics via doping donor ions

Colossal Dielectric Permittivity in (al+nb) Co-Doped Ba0.4Sr0.6TiO3 Ceramics

Double pentavalent (Sb5+, Nb5+) and trivalent (Sm3+, Y3+) co-doped Ti0.9Zr0.1O2 colossal dielectric permittivity multilayer ceramics for the miniaturization of the next-generation electronics

Reduce the low-frequency dielectric loss of (In0.5Nb0.5)0.05Ti0.95O2 ceramics by constructing insulating ZrO2 phase boundaries

High energy storage and colossal permittivity CdCu3Ti4O12 oxide ceramics

Columbite-rich Multiphase TiO2 Nanoceramic with Superior Mechanical and Dielectric Properties

Dielectric Responses of (Zn0.33Nb0.67) x Ti1- xO2 Ceramics Prepared by Chemical Combustion Process: DFT and Experimental Approaches

Microstructural Evolution and High-Performance Giant Dielectric Properties of Lu3+/Nb5+ Co-Doped TiO2 Ceramics

High dielectric permittivity and ultralow dielectric loss in Nb-doped SrTiO 3 ceramics

Defect engineering in rare‐earth‐doped BaTiO 3 ceramics: Route to high‐temperature stability of colossal permittivity

Low dielectric loss, colossal permittivity, and high breakdown electric field in Al-doped Y2/3Cu3Ti4O12 ceramics