In vivo biodegradation and biocompatibility of Mg-Zn alloys
Hai-rong Tao,Yan Zhang,Yao-hua He,Yao Jiang,Shao-xiang Zhang,Xiao-nong Zhang
DOI: https://doi.org/10.3969/j.issn.1673-8225.2009.12.005
2009-01-01
Abstract:BACKGROUND: Magnesium ion can accelerate growth of osteoblasts, but compatibility and in vivo degradation of Mg alloy remain still unknown. OBJECTIVE: To investigate the biocompatibility and in vivo degradation of Mg-Zn alloys as well as bone formation. DESIGN, TIME AND SETTING: A randomized controlled animal experiment was performed at the Animal Experimental Laboratory of the Sixth People’s Hospital of Shanghai Jiao Tong University between March and November 2008. MATERIALS: Mg-Zn alloys were provided by Shanghai Aoruiji Materials and Medical Technology Co., Ltd., containing 94% Mg and 6% Zn. Poly-L-lactide rods were provided by Jingtong Company. METHODS: A total of 48 New Zealand rabbits were randomly divided into Mg-Zn alloys group and poly-L-lactide rods group, with 24 rabbits for each group. The left femoral condyles were drilled (φ 0.45 cm × 1 cm) and separately implanted with Mg-Zn alloys and poly-L-lactide rods. MAIN OUTCOME MEASURES: The serum magnesium Mg2+ was measured in the Mg-Zn alloys group at 1 day pre-operatively, 1 day, 1, 2, 5, and 10 weeks post-operatively. During the same period, albumin, alkaline phosphatase, alanine transaminase, urea nitrogen, and urine creatinine were recorded in the two groups. Thereafter, the samples were photographed using X-ray at 3, 6, 12, and 18 weeks post-implantations, and then condyles of femur was obtained, decalcified, and stained using hematoxylin-eosin staining for analysis of bone mass. RESULTS: Serological indicators in the Mg-Zn alloys group were increased in the first week, but they were decreased from the second week, and there was no significant difference. In addition, there were also no significant differences in biochemical indicators between the two groups. X-ray examination showed that gas was produced surrounding Mg-Zn alloys after 3 weeks. New bones were found after 6 weeks, bone density was increased after 12 weeks, and gas was absorbed after 12 weeks. Otherwise, gas was not detected, but new bones were found in the poly-L-lactide rods group. New bones in the Mg-Zn alloys were more than poly-L-lactide rods group at 18 weeks (P < 0.05). CONCLUSION: New bones are formed when the Mg-Zn alloys are degraded in vivo, and the Mg-Zn alloys have good biocompatibility.