Abstract:The rapid degradation of magnesium (Mg)-based implants in physiological environment limits its clinical applications, and alloying treatment is an effective way to regulate the degradation rate of Mg-based materials. In the present study, three Mg alloys, including Mg-0.8Ca (denoted as ZQ), Mg-0.8Ca-5Zn-1.5Ag (denoted as ZQ71) and Mg-0.8Ca-5Zn-2.5Ag (denoted as ZQ63), were fabricated by alloying with calcium (Ca), zinc (Zn) and silver (Ag). The results obtained from electrochemical corrosion tests and in vitro degradation evaluation demonstrated that the three Mg alloys exhibited distinct corrosion resistance, and ZQ71 exhibited the lowest degradation rate in vitro among them. After addition of Zn and Ag, the antibacterial potential of Mg alloys was also enhanced. The in vitro cell experiments showed that all the three Mg alloys had good biocompatibility. After implantation in a rat femoral defect, ZQ71 showed significantly higher osteogenic activity and bone substitution rate than ZQ63 and ZQ, due to its higher corrosion resistance as well as the stimulatory effects of the released metallic ions. In addition, the average daily degradation rate of each Mg alloy in vivo was significantly higher than that in vitro, as could be due to the implantation site located in the highly vascularized trabecular region. Importantly, the correlations between the in vitro and in vivo degradation parameters of the Mg alloys were systematically analyzed to find out the potential predictors of the in vivo degradation performance of the materials. The current work not only evaluated the clinical potential of the three biodegradable Mg alloys as bone grafts but also provided a feasible approach for predicting the in vivo degradation behavior of biodegradable materials.

In vitro corrosion and cytocompatibility of Mg-Zn-Ca alloys coated with FHA

The in Vitro Indirect Cytotoxicity Test and in Vivo Interface Bioactivity Evaluation of Biodegradable FHA Coated Mg–Zn Alloys

In Vitro Degradation and Mechanical Integrity of Mg-Zn-Ca Alloy Coated with Ca-deficient Hydroxyapatite by the Pulse Electrodeposition Process.

In Vitro Corrosion and Cytocompatibility of ZK60 Magnesium Alloy Coated with Hydroxyapatite by a Simple Chemical Conversion Process for Orthopedic Applications

Corrosion Resistance and Biocompatibility Assessment of a Biodegradable Hydrothermal-Coated Mg-Zn-Ca Alloy: An in Vitro and in Vivo Study

In vitro and in vivo corrosion, mechanical properties and biocompatibility evaluation of MgF2-coated Mg-Zn-Zr alloy as cancellous screws

The Bioactivated Interfacial Behavior of the Fluoridated Hydroxyapatite-Coated Mg-Zn Alloy in Cell Culture Environments

In Vitro Degradation and Electrochemical Corrosion Evaluations of Microarc Oxidized Pure Mg, Mg-Ca and Mg-Ca-Zn Alloys for Biomedical Applications

In vitro responses of human bone marrow stromal cells to a fluoridated hydroxyapatite coated biodegradable Mg-Zn alloy.

In Vivo Degradation and Bone Response of A Composite Coating on Mg-Zn-Ca Alloy Prepared by Microarc Oxidation and Electrochemical Deposition

Study on the Corrosion Behavior in Vitro and Mechanical Properties of the FHA Coated Mg-Zn-Zr Alloy

In Vitro Corrosion and Cytocompatibility of A Microarc Oxidation Coating and Poly(L-Lactic Acid) Composite Coating on Mg-1li-1ca Alloy for Orthopedic Implants

Evaluation on the corrosion resistance, antibacterial property and osteogenic activity of biodegradable Mg-Ca and Mg-Ca-Zn-Ag alloys

Corrosion Resistance and Biocompatibility of Calcium Phosphate Coatings with a Micro-Nanofibrous Porous Structure on Biodegradable Magnesium Alloys

Growth, in Vitro Biodegradation and Cytocompatibility Properties of Nano-Hydroxyapatite Coatings on Biodegradable Magnesium Alloys

Osteoinduction Evaluation of Fluorinated Hydroxyapatite and Tantalum Composite Coatings on Magnesium Alloys

In Vitro and in Vivo Studies on As-Extruded Mg- 5.25Wt.%zn-0.6Wt.%ca Alloy As Biodegradable Metal

Electrodeposition of Ca-P coatings on biodegradable Mg alloy: in vitro biomineralization behavior

Preparation and characterization of a new biomedical Mg-Zn-Ca alloy

Microstructure and Properties of Hydroxyapatite-Containing Ceramic Coatings on Magnesium Alloys by One-Step Micro-Arc Oxidation