Transparent superhydrophobic coating for copper metal and study of surface morphology and antimicrobial characteristics

Akanksha Rajput,Abhilasha Mishra,Amena Ali,Rekha Goswami,Neha Bhatt

DOI: https://doi.org/10.1016/j.colsurfa.2023.133067

IF: 5.518

2024-01-08

Colloids and Surfaces A Physicochemical and Engineering Aspects

Abstract:Nowadays, copper is a widely used metal worldwide for various applications such as electronic materials, electrical circuits, ornamentals and decorative applications. Copper is widely known for its antimicrobial properties. Despite this fact, it is found to be susceptible to biocorrosion . To protect the copper metal from biocorrosion, hydrophobically modified silica nanoparticles were prepared by the sol gel process. The Prepared sol solution was characterized by Particle size analysis , transmission electron microscopy (TEM) and infrared spectroscopy. Modified silica nanoparticles coated on the copper substrate to obtain superhydrophobic surface. Surface morphology was observed by scanning electron microscopy (SEM), electron dispersive microscopy (EDX) and atomic force microscopy analysis (AFM). Wettability and antimicrobial activity of the copper surface were also studied. The average particle size was found to be 96 nm and the formation of silica nanoparticle in the sol was also confirmed by IR spectra. The Contact angle of coated copper was found 163.3 ̊compared to 66.6 ̊ of uncoated copper surface which confirms the superhydrophobic behavior of the coated surface. The presence of nanostructured surfaces was responsible for superhydrophobic behavior which was confirmed by SEM and AFM studies. The coated copper showed excellent antimicrobial characteristics against E-coli .

chemistry, physical
Effect of acid pickling treatment of stainless steel substrate on adhesion strength of electrodeposited copper coatings using non-cyanide electrolyte

Naveen Bharadishettar,K. Udaya Bhat

DOI: https://doi.org/10.1016/j.ijadhadh.2023.103518

IF: 3.848

2023-09-30

International Journal of Adhesion and Adhesives

Abstract:In recent years, copper-based antimicrobial coatings have gained popularity in healthcare and public recreation facilities. The morphology, topography, and adhesion strength are decisive properties for copper coatings to have long-term antimicrobial effectiveness in hospital environments. This work explores the effect of multistage acid pickling treatment of AISI 304 stainless steel substrate on the adhesion strength of the copper coating. The copper coating was obtained by electrodeposition using an alkaline non-cyanide electrolyte. After the fourth stage of acid pickling, the copper coating had an excellent adhesion strength, up to 9 MPa. Glow discharge optical emission spectroscopy (GDOES) examination revealed no oxide scales or other contaminants on the SS surface after the fourth (final) stage of acid pickling. Using a non-contact optical profilometer, it was observed that the roughness of the substrate increased with each stage of the pickling treatment. The surface topography analysis confirms the increased density of the interlocking sites, which favors the adhesion of the coating. On the other hand, the microstructure of the copper coating showed a cauliflower-like morphology with an average nodule size of 28 nm. Transmission electron microscopy confirmed that the coatings have nano-scaled crystallites with internal twins inside the grains of copper coatings.

materials science, multidisciplinary,engineering, chemical
Distinctive Effects of Surface Roughness and Ions Release on the Bacterial Adhesion and Inactivation of Textured Copper Oxide Surfaces

Akram Alhussein,Lylia Aouchiche,Abdelhamid Hmima,Delphine Retraint,Sami Rtimi

DOI: https://doi.org/10.3390/coatings13020454

IF: 3.236

2023-02-17

Coatings

Abstract:In this manuscript, we studied the effect of additive manufacturing pretreatment on bacterial adhesion and inactivation on copper-based interfaces. Sandblasting, mirror polishing and Surface Mechanical Attrition Treatment (SMAT) at high or low energies have been employed to modify the substrate's (316L stainless steel) roughness. The pretreated substrates were coated with thin copper films using magnetron sputtering. The thin copper films' composition and antibacterial activities were first optimized by being deposited on an Si wafer. We showed that the surface roughness profile influenced bacterial adhesion in the dark. Bacterial inactivation was monitored under indoor light. Stereomicroscopy imaging showed live/dead bacterial cells on the coated substrates. Scanning electron microscopy (SEM) showed homogeneous coating growths of copper with a columnar texture. The chemical composition of the deposited Cu thin films was carried out by Energy Dispersive X-ray Spectroscopy (EDX) and showed a uniform distribution of copper and oxygen, revealing the formation of copper oxides (CuxO). The oxygen content of the sputtered films varied from 7.8 to 25%, justifying the semi-conductor behavior of the thin films under indoor light. The crystallographic structure of the sputtered thin films was investigated using X-ray diffraction (XRD), showing the cubic Cu peaks and characteristic peaks of Cu2O. The Cu peaks at 2θ values of 43.28°, 50.40° and 74.81° were attributed to the (111), (200) and (220) planes, respectively. The use of genetically modified bacteria (without porins) allowed the rationalization of the predominant effect of the extracellular bacterial inactivation compared to that of intracellular bacterial inactivation through ion release and diffusion.

materials science, multidisciplinary,physics, applied, coatings & films
Studying the Effect of Magnetron Copper Deposition on the Surface Topography of Biodegradable Antibacterial Coating

Maratuly Bauyrzhan,Bagdat Nurlanovich Azamatov,Alexey Vladimirovich Jes

DOI: https://doi.org/10.18502/ajmb.v16i3.15743

Abstract:Background: The surface properties of the materials used significantly influence the success and longevity of medical implants. Increasing surface roughness promotes osteoblast activity and osseointegration, while biodegradable materials such as copper have shown potential for antimicrobial applications. However, the effect of coating parameters on surface topography is not well investigated. Methods: Sputtering of copper was performed using EPOS-PVD-440 system (Zeleno-grad, Russia). The samples were examined by Scanning Electron Microscopy (SEM) with subsequent image processing in Mountains software (Digital Surf). Antibacterial efficacy was evaluated against Staphylococcus aureus by measuring the zone of inhibition. Additionally, copper ion release was monitored over time to assess its correlation with changes in surface topography. Results: Higher sputtering currents increased surface roughness and particle size, with a significant release of copper ions within the first 24 hr of immersion. Samples sputtered at higher currents exhibited coarser grain structures. The release of copper ions in the simulated biological environment led to further changes in surface topography, highlighting the critical influence of sputtering parameters on coating properties. Conclusion: Optimizing magnetron copper deposition parameters enhances the surface topography and antibacterial effectiveness of biodegradable coatings on implants.
Copper As an Antibacterial Agent for Human Pathogenic Multidrug Resistant Burkholderia Cepacia Complex Bacteria

Muhammad Ibrahim,Fang Wang,Miao-miao Lou,Guan-lin Xie,Bin Li,Zhu Bo,Gou-qing Zhang,He Liu,Abdul Wareth

DOI: https://doi.org/10.1016/j.jbiosc.2011.08.017

IF: 3.185

2011-01-01

Journal of Bioscience and Bioengineering

Abstract:The Burkholderia cepacia complex (Bcc) consists of 17 closely related multidrug resistant bacterial species that are difficult to eradicate. Copper has recently gained attention as an antimicrobial agent because of its inhibitory effects on bacteria, yeast, and viruses. The objective of this study was to evaluate the antibacterial activity of copper surfaces and copper powder against members of the B. cepacia complex. The antibacterial activity of different copper surfaces was evaluated by incubating them with Bcc strain suspensions (5×10(7)cfu/ml). The bacterial survival counts were calculated and the data for various copper surfaces were compared to the data for stainless steel and polyvinylchloride, which were used as control surfaces. The antibacterial activity of copper powder was determined with the diffusimetrical technique and the zone of inhibition was evaluated with paper disks. A single cell gel electrophoresis assay, staining assays, and inductively coupled plasma mass spectroscopy were performed to determine the mechanism responsible for the bactericidal activity. The results showed a significant decrease in the viable bacterial count after exposure to copper surfaces. Moreover, the copper powder produced a large zone of inhibition and there was a significantly higher influx of copper ions into the bacterial cells that were exposed to copper surfaces compared to the controls. The present study demonstrates that metallic copper has an antibacterial effect against Bcc bacteria and that copper adversely affects the bacterial cellular structure, thus resulting in cell death. These findings suggest that copper could be utilized in health care facilities to reduce the bioburden of Bcc species, which may protect susceptible members of the community from bacterial infection.
Investigation on the effect of nickel and nickel-chromium alloy pulse current plating on copper substrate

Canute Sherwin,Sudip Chakraborty,K. Raju,Suma Bhat,Sudheendra P. Hebbar

DOI: https://doi.org/10.1080/00202967.2023.2208437

2023-06-02

Transactions of the IMF

Abstract:In the present study, nanocrystalline nickel (Ni) and nickel-chromium (Ni-Cr) alloy coatings were developed on copper (Cu) substrate using pulse current. The pulse current parameters include a cycle time of 240 milliseconds at a duty cycle of 0.5 and 4.17 Hz frequency. The surface morphology, texture, hardness, scratch resistance and porosity were investigated for different coatings developed by pulse plating. Energy Dispersive Spectroscopy (EDS) analysis revealed good quality Ni and Ni-Cr alloy coatings developed on the copper substrate. The peak current of the pulse has been observed to have an impact on the coating weight and thickness. The micrographs of the coatings explored under Field Emission Scanning Electron Microscopy (FESEM), depict uniform coatings consisting of fine primary and coarse secondary granules of Ni and Cr. The hard primary and secondary Ni granules deposited on the surface of Cu increase its hardness, corrosion and wear resistance. Further, it was observed that the Ni-Cr alloy plated samples are harder and less porous in nature compared to Ni plated samples.

electrochemistry,metallurgy & metallurgical engineering,materials science, coatings & films
Electrochemical behavior and electro-crystallization mechanism of Cu-Ni/Nano-Al 2 O 3 coating with a deposition current density dependence

Yi Zhang,Jingjing Zhang,Zhiqiang Wang,Jingxiao Liu

DOI: https://doi.org/10.1016/j.jallcom.2023.169988

IF: 6.2

2023-04-07

Journal of Alloys and Compounds

Abstract:In this work, preparation of Cu-Ni/Nano-Al 2 O 3 composite coating with (111)-preferred orientation on the surface of the H64 brass via electrodeposition technique. Variation of the deposition current density was found to play a key role in the control of the microstructure and strongly influence the corrosion resistance of the composite coating. Electrochemical impedance spectroscopy results indicated that the increase of nano-alumina content in composite coating is caused by the change of polarization mode. Under different current densities, the Ni (111) plane is only preferred orientation and the relative texture coefficient reaches the highest value of 54.36% at 5 A•dm -2 . The crystallite size of these coatings is about 10–55 nm dependent on current density, and high current density could refine the size. The microstructure of the coating changed from cauliflower to spherical with increasing deposition current density. Moreover, the Cu-Ni/Nano-Al 2 O 3 composite coating obtained at 5 A•dm -2 increased the polarization resistance and coating resistance of the H64 brass by about 50% and 83%, respectively. The corrosion potential ( E corr ) of Cu-Ni/Nano-Al 2 O 3 composite coating is shifted towards the nobler direction from -1.191 V to -0.063 V (Ag/AgCl) with the current density increases. The corrosion mechanism of Cu-Ni/Nano-Al 2 O 3 composite coating has gone through two stages corresponding to two-time and three-time constant of EEC models, respectively. The Cu-Ni/Nano-Al 2 O 3 has large potential merits in field of corrosion.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
Copper Oxide Electrochemical Deposition to Create Antiviral and Antibacterial Nanocoatings

Anna Kusior,Julia Mazurkow,Piotr Jelen,Maciej Bik,Sada Raza,Mateusz Wdowiak,Kostyantyn Nikiforov,Jan Paczesny

DOI: https://doi.org/10.1021/acs.langmuir.4c00642

IF: 3.9

2024-07-23

Langmuir

Abstract:The impact of the reaction environment on the formation of the polycrystalline layer and its biomedical (antimicrobial) applications were analyzed in detail. Copper oxide layers were synthesized using an electrodeposition technique, with varying additives influencing the morphology, thickness, and chemical composition. Scanning electron microscopy (SEM) images confirmed the successful formation of polyhedral structures. Unmodified samples (CuL) crystallized as a mixture of copper oxide (I) and (II), with a thickness of approximately 1.74 μm. The inclusion of the nonconductive polymer polyvinylpyrrolidone (PVP) during synthesis led to a regular and compact CuO-rich structure (CuL-PVP). Conversely, adding glucose resulted in forming a Cu2O-rich nanostructured layer (CuL-D(+)G). Both additives significantly reduced the sample thickness to 617 nm for CuL-PVP and 560 nm for CuL-D(+)G. The effectiveness of the synthesized copper oxide layers was demonstrated in their ability to significantly reduce the T4 phage titer by approximately 2.5-3 log. Notably, CuL-PVP and CuL-D(+)G showed a more substantial reduction in the MS2 phage titer, achieving about a 5-log decrease. In terms of antibacterial activity, CuL and CuL-PVP exhibited moderate efficacy against Escherichia coli, whereas CuL-D(+)G reduced the E. coli titer to undetectable levels. All samples induced similar reductions in Staphylococcus aureus titer. The study revealed differential susceptibilities, with Gram-negative bacteria being more vulnerable to CuL-D(+)G due to its unique composition and morphology. The antimicrobial properties were attributed to the redox cycling of Cu ions, which generate ROS, and the mechanical damage caused by nanostructured surfaces. A crucial finding was the impact of surface composition rather than surface morphology on antimicrobial efficacy. Samples with a dominant Cu2O composition exhibited potent antibacterial and antiviral properties, whereas CuO-rich materials showed predominantly enhanced antiviral activity. This research highlights the significance of phase composition in determining the antimicrobial properties of copper oxide layers synthesized through electrodeposition.
An interview with Michael Fordham. Interview by Paul Roazen.

M. Fordham

DOI: https://doi.org/10.1111/J.0021-8774.2005.00506.X

2005-02-01

Journal of Analytical Psychology

Abstract:In the course of early interviews on the history of psychoanalysis, I saw Michael Fordham in the late summer of 1965. We concentrated primarily on the differences between Freud and Jung, as well as the characteristic distinctions between the two schools that they founded. Fordham also talked about some of his personal contacts with Jung.
Effect of current density on the texture, residual stress, microhardness and corrosion resistance of electrodeposited chromium coating

Jinghan Yang,Pengfei Ji,Jin Zhang,Weisheng Xu,Jinchao Jiao,Yong Lian,Liming Jiang,Biliang Zhang

DOI: https://doi.org/10.1016/j.surfcoat.2023.129868

IF: 4.865

2023-08-02

Surface and Coatings Technology

Abstract:Textures and residual stresses are generated during electrodeposition of chromium coatings, which directly affect the performance of the coating. In this work, the variations of texture, hydrogen content, residual stress, microhardness and corrosion resistance of chromium deposited from hexavalent [Cr(VI)] chromium bath using direct current deposited technique were investigated. Electrodeposition experiments were carried out on the low carbon steel substrate by varying the key variable current density. The macrotexture of the coatings was studied by XRD. The crystal orientation and dislocation density were analyzed by EBSD. Residual stress was measured by the indentation method. The research demonstrated that a single preferred orientation on the (222) plane was found at current densities of 20 A/dm 2 , 35 A/dm 2 and 50 A/dm 2 . At 40 A/dm 2 , a mixed preferred orientation on the (222) + (211) planes was discovered. Furthermore, the formation of the chromium coating texture was affected by the variation of hydrogen content, for higher hydrogen promoting grain growth along the (222) crystal plane. Notably, the microstructure-property relationship was developed. At the single preferred orientation of (222) plane, the corrosion resistance was more favorable. At the mixed preferred orientation of (222) + (211) planes, the coating surface achieved higher microhardness, but formed higher residual stress and more microcracks. Moreover, the better electroplating parameter was proposed. At 35 A/dm 2 , the coating had the fewer microcracks and the better overall performance. The higher microhardness of 753 HV was found. The more favorable corrosion resistance was discovered, with the breakdown potential and passive current density of 804.7 mV and 2.220 × 10 −6 A/dm 2 . The lower residual stress of 61 MPa was found, which was about 81 % lower than the maximum stress. It was significant in industry for the enhancement of the service life of substrate and the optimization of the chromium coating process.

physics, applied,materials science, coatings & films
Study of the Effect of Current Density on the Metallurgical Properties of AlFeCrNiTi High Entropy Alloy Coating Produced by Pulse Plating

Zahra Shojaei,Gholam Reza Khayati,Esmaeel Darezereshki,Khayati, Gholam Reza

DOI: https://doi.org/10.1007/s12540-024-01767-w

IF: 3.451

2024-08-10

Metals and Materials International

Abstract:Pulsed current electrodeposition was used to deposit a novel AlFeCrNiTi high entropy alloy coating on copper. As a first step, cyclic voltammetry was used to determine the minimum current required to reduce all metal ions on the substrate. Afterward, 150, 250 and 350 mA/cm 2 current densities were investigated for their effects on coating microstructure, corrosion, mechanical, and magnetic properties. SEM, EDS, and XRD studies were conducted to examine the coatings morphology, chemical composition, and phase analysis. A microhardness, wear, VSM, DC polarization, and EIS techniques were used to study the mechanical, magnetic, and corrosion properties of the coatings. As a result of EDS, XRD, and thermodynamic calculations, AlFeCrNiTi high entropy alloy coating with the BCC + FCC combined structure has been confirmed. Moreover, it was determined from other tests that coatings with a uniform structure, maximum microhardness (520 HV) and charge transfer resistance (4306 Ω.cm 2 ), the lowest corrosion current density (0.088 μ A/cm 2 ), and favorable wear properties were obtained at a pulsed electroplating current density of 250 mA/cm 2 . Due to the higher nickel and iron content of the coating created at 150 mA/cm 2 , maximum saturation magnetization was achieved (105.64 emu/g).

materials science, multidisciplinary,metallurgy & metallurgical engineering
Construction of a TiO2/Cu2O multifunctional coating on Ti-Cu alloy and its influence on the cell compatibility and antibacterial properties

Shuo Liu,Ziming Zhang,Jiaqi Zhang,Gaowu Qin,Erlin Zhang

DOI: https://doi.org/10.1016/j.surfcoat.2021.127438

IF: 4.865

2021-09-01

Surface and Coatings Technology

Abstract:Inflammation and infection caused by implants are serious problems in the clinical application of titanium and titanium alloy. Titanium copper alloy has shown strong antibacterial properties, but the surface bioactivity is still necessary to be modification to improve biocompatibility. In this paper, a TiO2/Cu2O multifunctional coating was prepared on Ti-5Cu alloy by an anodic oxidation process in order to enhance the surface bioactivity without affecting the antibacterial ability. The surface physical and chemical properties of the anodized Ti-Cu alloys were tested by X-ray diffraction (XRD), X-ray photo-electron spectroscopy (XPS), scanning electron microscopy (SEM), Vickers hardness tester, contact angle tester and laser confocal microscope, and the corrosion properties were studied by inductively coupled plasma mass spectrometer and electrochemical workstation. The results have shown that the roughness, the hydrophilicity, the copper ion release the corrosion resistance were increased by the anodization in a voltage dependent way. The effect of the anodization was evaluated on the antibacterial properties and cell bioactivity. It was shown that pure titanium did not have antibacterial properties after the anodization. However, the anodization significantly improved the antibacterial properties of titanium copper alloy due to the formation of TiO2/Cu2O coating. No cytotoxicity was found on Ti-5Cu alloys and the anodized Ti-5Cu alloys but the treatment accelerated the cell adhesion. It was suggested that anodization treatment might be a potential surface biomodification method for the clinical application of titanium copper alloys.

physics, applied,materials science, coatings & films
Antibacterial Anodic Aluminium Oxide-Copper Coatings on Aluminium Alloys: Preparation and Long-Term Antibacterial Performance

Jiahuan Chen,Zhen He,Jiaming Liu,Yuxin Wang,Michael Hodgson,Wei Gao

DOI: https://doi.org/10.2139/ssrn.4310488

2022-01-01

SSRN Electronic Journal

Abstract:Anodic aluminium oxide-copper (AAO-Cu) coatings were prepared on the aluminium (Al) alloy substrates to attain excellent antibacterial performance and mechanical stability. The nanoporous AAO interlayer was obtained by anodic oxidation with an outer Cu layer deposited by electroplating. The intermediate zone (~2 μm thick) of the AAO-Cu coating plays a significant role in the coating properties. The interlocking effect in the AAO-Cu intermediate zone significantly enhances the coating adhesion and curbs the coating defoliation. The antibacterial tests show that the AAO-Cu zone provides excellent antibacterial ability even when the outer Cu coating was removed. The sustained antibacterial rate of the AAO-Cu intermediate zone against E. coli exceeded 95%. The Cu ions released from the embedded Cu in the nanoporous AAO structure ensure a long-term antibacterial capability. This coating system can be promoted in a large wide range of antibacterial products in public.

English Else
Effect of deposition time of sputtering Ag-Cu thin film on mechanical and antimicrobial properties

A. Purniawan,R. Hermastuti,H. Purwaningsih,T. M. Atmono

DOI: https://doi.org/10.1063/1.5030230

2018-01-01

AIP Conference Proceedings

Abstract:Metallic implants are important components in biomedical treatment. However, post-surgery infection often occurs after installation of implant. The infections are usually treated by antibiotics, but it still causes several secondary problems. As a prevention treatment, the surgical instruments and implants must be in a sterile condition. This action is still not optimal too because the material still can attract the bacteria. From material science point of view, it can be anticipated by developing a type of material which has antibacterial properties or called antimicrobial material. Silver (Ag) and Copper (Cu) have antimicrobial properties to prevent the infection. In this research, the influence of deposition time of Ag-Cu thin film deposition process as antimicrobial material with Physical Vapor Deposition (PVD) RF Sputtering method was analyzed. Deposition time used were for 10, 15 and 20 minutes in Argon gas pressure around 3 x 10-2 mbar in during deposition process. The morphology and surface roughness of Ag-Cu thin film were characterized using SEM and AFM. Based on the results, the deposition time influences the quality morphology that the thin films have good homogeneity and complete structure for longer deposition time. In addition, from roughness measurement results show that increase deposition time decrease the roughness of thin film. Antimicrobial performance was analyzed using Kirby Bauer Test. The results show that all of sample have good antimicrobial inhibition. Adhesion quality was evaluated using Rockwell C Indentation Test. However, the results indicate that the Ag-Cu thin film has low adhesion strength.

English Else
Effect of Biological Contamination of Copper Surfaces with Extreme Wettability on Their Antibacterial Properties

F. S. Omran,V. V. Kaminsky,K. A. Emelyanenko,A. M. Emelyanenko,L. B. Boinovich

DOI: https://doi.org/10.1134/s1061933x23600641

2023-10-12

Colloid Journal

Abstract:Bacterial health care-associated infections (HCAI) are one of the acute problems of modern healthcare. One of the promising directions for solving this problem is the development of materials that either have a bactericidal effect against HCAI pathogens or prevent the transmission of bacteria deposited on their surface by patients and staff contacts with such surfaces. In this work, the antibacterial effectiveness of copper contact surfaces with different wettability was investigated. Particular attention was paid to studying the effect on this efficacy of surface contamination by both human contact sweat and bacterial life-supporting substances, using a peptone solution as an example. Due to the high cost of copper, the possibility of replacing bulk copper material with less expensive sprayed copper-coated materials was also investigated. The test results showed that the bactericidal efficacy against Staphylococcus aureus strain of both control copper and superhydrophilic copper samples, as well as of sputtered copper films, is close to 100% and almost unchanged after contamination with peptone solution or sweat excretions. Superhydrophobic copper surfaces have less bactericidal efficacy, but due to the non-wettability effect and low cell adhesion to such surfaces, they remain uncontaminated longer and thus also promote reducing the transmission of infections through the touch surfaces made of them.

chemistry, physical
Influence of copper distribution in thermally sprayed Cu-bearing coatings on corrosion and microbial activity

Hongshou Huang,Surinder Singh,Albert Juhasz,Anthony Roccisano,Andrew Siao Ming Ang,Nikki Stanford

DOI: https://doi.org/10.1016/j.surfcoat.2024.130430

IF: 4.865

2024-02-01

Surface and Coatings Technology

Abstract:Microbiologically influenced corrosion (MIC) inside steel pipes used for natural gas transmission is a persistent challenge. In this study, antimicrobial copper (Cu)-bearing coatings were introduced as a viable solution to address the issue. To enhance corrosion resistance while maintaining enduring antimicrobial properties of proposed coatings, two innovative microstructural design strategies were proposed by tailoring Cu distributions: composite coatings and retaining Cu in solid solution. Implementing these strategies, two types of Cu-containing coatings, stainless steel (SS)-Cu composite coatings and Monel 400 coatings with Cu in solid solution were deposited on steel substrates using high velocity oxy-fuel (HVOF) and wire arc spray (WAS) techniques. The influence of Cu distribution on corrosion resistance, long-term Cu-ion dissolution behavior, and antimicrobial properties of these coatings were systematically investigated. Findings unveiled that irrespective of the employed thermal spray technique, SS-Cu composite coatings exhibited preferential dissolution of Cu due to micro-galvanic effects between Cu and the more noble stainless-steel laminates, significantly enhancing their short-term antimicrobial properties against three different bacterial species. Antimicrobial durability, assessed through long-term salt spray tests, showcased the potential of composite coatings for sustained Cu-ion release. However, localized corrosion propagation toward the substrate led to significantly expedited coating failure. In contrast, WAS Monel coatings, characterized by Cu in solid solution, demonstrated uniform-dominated corrosion but with enhanced corrosion resistance. Despite reduced antimicrobial efficacy, WAS Monel showed promise for long-term protection against MIC in pipeline environments, striking a balance between corrosion resistance and antimicrobial effectiveness.

physics, applied,materials science, coatings & films
Serum IL-16, not IL-15, was elevated in early second trimester of pregnancy in women who subsequently developed preeclampsia.

Shi-ming Lu,Han-zhi Wang,Yaping Shi,Yali Sun,Hefeng Huang,M. Dong

DOI: https://doi.org/10.1016/J.CCA.2007.04.022

2007-08-01

Abstract:
Tetracycline-induced bile duct paucity and prolonged cholestasis.

C. Hunt,K. Washington

DOI: https://doi.org/10.1016/0016-5085(94)90830-3

IF: 29.4

1994-12-01

Gastroenterology

Abstract:
A novel nickel-copper alternating-deposition coating with excellent tribological and antibacterial property

Ying Wang,Xiaoxing Lu,Ningyi Yuan,Jianning Ding

DOI: https://doi.org/10.1016/j.jallcom.2020.156222

IF: 6.2

2020-12-01

Journal of Alloys and Compounds

Abstract:In order to enhance the tribological and antimicrobial properties of nickel coating and the substrate, a novel nickel-copper alternately deposited coating was designed in this work. The nickel-copper alternate layered coatings (Ni–Cu, Cu–Ni) and the pure nickel and the pure copper coating were prepared on mild steel by electroplating in two independent plating solutions, respectively. The microstructure of the four coatings was observed by the scanning electron microscopy, and the composition of the coatings was determined by the energy dispersive spectrometer and X-ray diffractometer. The tribological test of four coatings were carried out under different loads. The results showed that the Ni–Cu coating displayed good wear resistance and load-carrying capacity and the outer copper layer could protect the inner nickel layer well. When the load was up to 2 N, the wear rate of Ni–Cu coating was only 5% higher than that of Ni coating, but the friction coefficient was 0.05 much lower than that of nickel coating. The antibacterial properties of four kinds of coatings against Escherichia coli and Bacillus subtilis were studied respectively. It was found that Ni–Cu coating displayed excellent antibacterial activity compared with Ni coating. At the same time, compared to B. subtilis, Ni–Cu coating was more likely to inactivate E. coli because of its thinner cell membrane.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
Correction: Environmentally Induced Transgenerational Epigenetic Reprogramming of Primordial Germ Cells and the Subsequent Germ Line

M. Skinner,Carlos Guerrero-Bosagna M. Haque,E. Nilsson,R. Bhandari,J. McCarrey

DOI: https://doi.org/10.1371/ANNOTATION/7683BB48-85DB-4C7E-87C0-304A7D53A587

IF: 3.7

2013-07-30

PLoS ONE

Abstract:

[The current situation of tuberculosis in Spain].

Transparent superhydrophobic coating for copper metal and study of surface morphology and antimicrobial characteristics

Effect of acid pickling treatment of stainless steel substrate on adhesion strength of electrodeposited copper coatings using non-cyanide electrolyte

Distinctive Effects of Surface Roughness and Ions Release on the Bacterial Adhesion and Inactivation of Textured Copper Oxide Surfaces

Studying the Effect of Magnetron Copper Deposition on the Surface Topography of Biodegradable Antibacterial Coating

Copper As an Antibacterial Agent for Human Pathogenic Multidrug Resistant Burkholderia Cepacia Complex Bacteria

Investigation on the effect of nickel and nickel-chromium alloy pulse current plating on copper substrate

Electrochemical behavior and electro-crystallization mechanism of Cu-Ni/Nano-Al 2 O 3 coating with a deposition current density dependence

Copper Oxide Electrochemical Deposition to Create Antiviral and Antibacterial Nanocoatings

An interview with Michael Fordham. Interview by Paul Roazen.

Effect of current density on the texture, residual stress, microhardness and corrosion resistance of electrodeposited chromium coating

Study of the Effect of Current Density on the Metallurgical Properties of AlFeCrNiTi High Entropy Alloy Coating Produced by Pulse Plating

Construction of a TiO2/Cu2O multifunctional coating on Ti-Cu alloy and its influence on the cell compatibility and antibacterial properties

Antibacterial Anodic Aluminium Oxide-Copper Coatings on Aluminium Alloys: Preparation and Long-Term Antibacterial Performance

Effect of deposition time of sputtering Ag-Cu thin film on mechanical and antimicrobial properties

Effect of Biological Contamination of Copper Surfaces with Extreme Wettability on Their Antibacterial Properties

Influence of copper distribution in thermally sprayed Cu-bearing coatings on corrosion and microbial activity

Serum IL-16, not IL-15, was elevated in early second trimester of pregnancy in women who subsequently developed preeclampsia.

Tetracycline-induced bile duct paucity and prolonged cholestasis.

A novel nickel-copper alternating-deposition coating with excellent tribological and antibacterial property