Abstract:Experimental set‐up showing the mechanical testing of laminated composites under fire conditions. This study explores the effects of critical temperature conditions on carbon fiber‐reinforced Poly Phenylene Sulfide (PPS) laminates, focusing on the coupling between thermal and mechanical behaviors. The thermo‐mechanical behavior of angle‐ply laminates is examined under both homogeneous (thermal decomposition and deformation/damage) and heterogeneous (fire) conditions following three primary objectives: (i) Investigate the impact of temperature distribution on the formation of porosities within the composite, considering their significance in thermal transfer and stress concentration—(ii) Evaluate the changes in residual mechanical behavior and properties under tension due to thermally‐induced damage—(iii) Improve the understanding of the interactions between severe thermal exposures and the mechanical behavior. X‐ray tomographic analyses and tensile tests were conducted to achieve these goals. Porosities resulting from thermal damage are identified as a key factor affecting the structural integrity of C/PPS laminates for high‐temperature applications. Mechanical testing reveals that the porosity content significantly reduces the tensile properties (axial stiffness and strength). Under homogeneous temperature conditions, the decrease in the tensile properties is significant up to Tonset (465°C) from which both the axial strength and stiffness dramatically decrease by −75 and −50%, respectively. As exposed to a kerosene flame during 60 s, corresponding to an aggression of 115 kW/m2 on one face of the laminates, the retention of the residual tensile properties remains good (−12% and −22% in stiffness and strength respectively), despite the dramatic decomposition of the polymer matrix. This can be explained from the stress redistribution from the exposed to the back face, and from the role of thermal insulator played by porosities. Highlights Carbon fibers/PPS laminates were subjected to severe thermal aggressions The formation of thermally‐induced porosities is studied A homogeneous aggression significantly decrease the tensile properties (−75%) Once the PPS matrix is severely decomposed, the load transfer is not possible After a 60 s flame exposure, the retention of tensile properties is good (−20%)

In situ interlaminar shear behavior of carbon fibers reinforced polymer composites exposed to severe thermal aggressions: PPS versus epoxy laminates

Comparison of the in situ compressive behavior of carbon fibers woven ply laminates exposed to one‐sided heat flux: Thermoplastic versus thermosetting composites

Tensile behavior of angle ply carbon reinforced PPS laminates under severe thermal aggressions: Homogeneous and heterogeneous temperature conditions

About the influence of high temperature or fire testing conditions on the tensile behavior of carbon reinforced poly phenylene sulfide laminates

About the influence of a thermal aggression on the tensile behaviour of hybrid PEEK thermoplastic laminates

Determination of the tensile residual properties of a wound carbon/epoxy composite first exposed to fire

Effects of high temperature and strain rate on the impact-induced inter-laminar shear behavior of plain woven CF/PEEK thermoplastic composites

Time-dependent damage development during creep in carbon woven-ply polyphenylene sulfide laminates above the glass transition temperature

Thermal decomposition study of carbon fiber-reinforced polyphenylene sulfide at high heating rates met under fire exposure

Influence of strain rate and temperature on mechanical properties of carbon woven-ply PPS thermoplastic laminates under dynamic compression

Damage development in woven carbon fibre thermoplastic laminates with PPS and PEEK matrices: A comparative study

Low velocity impact and pseudo-ductile behaviour of carbon/glass/epoxy and carbon/glass/PMMA hybrid composite laminates for aircraft application at service temperature

Tensile impact behaviors and damage mechanism of woven carbon fiber-reinforced-polymer laminates considering adiabatic shear band

Effect of temperature on flexural and interlaminar shear strength properties of carbon‐epoxy composites: Experiment and modeling

Evaluation of Inter-Laminar Shear Performance of Carbon Fiber-Reinforced Composite under Quasi-Static and High-Strain-Rate Loading

Characteristics of in-situ automated fiber placement carbon-fiber-reinforced low-melt polyaryl ether ketone laminates part 1: Manufacturing influences

Mechanical Properties of High-Temperature Fiber-Reinforced Thermoset Composites with Plain Weave and Unidirectional Carbon Fiber Fillers

Low-Velocity Impact Resistance and Compression After Impact Strength of Thermoplastic Nanofiber Toughened Carbon/Epoxy Composites with Different Layups

Interlaminar Stress and Damage Mechanism of Thermoplastic Composite Laminates

The effect of laser assisted tape placement processing conditions on microstructural evolution, residual stress and interlaminar shear strength of carbon fibre/PEEK laminates

Effect of isothermal heat treatment on crystallinity, tensile strength and failure mode of CF/PPS laminate