Abstract:With the goal of improving processability of imide oligomers and achieving of high temperature carbon fiber composite, a series of Thermosetting Matrix Resin solutions (TMR) were prepared by polycondensation of aromatic diamine (3,4′-oxybisbenzenamine, 3,4-ODA) and diester of biphenylene diacid (BPDE) using monoester of 4-phenylethynylphthalic acid (PEPE) as end-capping agent in ethyl alcohol as solvent to afford phenylethynyl-endcapped poly(amic ester) resins with calculated molecular weight (Calc’d Mw) of 1500–10,000. Meanwhile, a series of reactive diluent solutions (RDm) with Calc’d Mw of 600–2100 were also prepared derived from aromatic diamine (4,4′-oxybisbenzenamine, 4,4-ODA), diester of asymmetrical biphenylene diacid (α-BPDE) and monoester of 4-phenylethynylphthalic acid (PEPE) in ethyl alcohol. Then, the TMR solution was mixed with the RDm solution at different weight ratios to afford a series of A-staged thermosetting blend resin (TMR/RDm) solutions for carbon fiber composites. Experimental results demonstrated that the thermosetting blend resins exhibited improved melt processability and excellent thermal stability. After being thermally treated at 200 °C/1 h, the B-staged TMR/RDm showed very low melt viscosities and wider processing window. The minimum melt viscosities of ≤50 Pa·s was measured at ≤368 °C and the temperature scale at melt viscosities of ≤100 Pa·s were detected at 310–390 °C, respectively. The thermally cured neat resins at 380 °C/2 h showed a great combination of mechanical and thermal properties, including tensile strength of 84.0 MPa, elongation at breakage of 4.1%, and glass transition temperature (Tg) of 423 °C, successively. The carbon fiber reinforced polyimide composite processed by autoclave technique exhibited excellent mechanical properties both at room temperature and 370 °C. This study paved the way for the development of high-temperature resistant carbon fiber resin composites for use in complicated aeronautical structures.

Mechanical Properties of High-Temperature Fiber-Reinforced Thermoset Composites with Plain Weave and Unidirectional Carbon Fiber Fillers

Comparison of the in situ compressive behavior of carbon fibers woven ply laminates exposed to one‐sided heat flux: Thermoplastic versus thermosetting composites

Optimizing the Thermal Properties of Fiber Reinforced Phthalonitrile Composites

Improved Melt Processabilities of Thermosetting Polyimide Matrix Resins for High Temperature Carbon Fiber Composite Applications

Evolution of strain-rate dependent compressive failure behavior of ceramifiable FRP composites at high temperature conditions

About the influence of high temperature or fire testing conditions on the tensile behavior of carbon reinforced poly phenylene sulfide laminates

The effect of heat-treatment temperature (HTT) on the carbon matrix development of both polyarylacetylene-and phenolic-derived carbon–Carbon (C/C) composites

The Out-of-Plane Compression Response of Woven Thermoplastic Composites: Effects of Strain Rates and Temperature

Development of the forming limit diagram for fiber-reinforced thermoplastic composites and its temperature effect

High-content continuous carbon fibers reinforced PEEK matrix composite with ultra-high mechanical and wear performance at elevated temperature

Thermomechanical Behavior and Microstructure Properties of Carbon Fiber Reinforced Polymer at Elevated Temperatures

High-Temperature Effect on the Tensile Mechanical Properties of Unidirectional Carbon Fiber-Reinforced Polymer Plates

Effects of high temperature and strain rate on the impact-induced inter-laminar shear behavior of plain woven CF/PEEK thermoplastic composites

Failure Behavior And Performance Analysis Of Hybrid-Fiber Reinforced Paek Composites At High Temperature

Evaluation of Tensile properties of FRP Composite Laminates under Varying Strain Rates and Temperatures

The effects of temperature and hygrothermal aging on the properties of CF/PA6 composite and its compression failure mechanisms

Experimental investigation on low‐velocity impact performance of carbon fiber reinforced polyether ether ketone thermoplastic composite materials in room and elevated temperature

Low velocity impact and pseudo-ductile behaviour of carbon/glass/epoxy and carbon/glass/PMMA hybrid composite laminates for aircraft application at service temperature

Elevated temperature effect on tension fatigue behavior and failure mechanism of carbon/epoxy 3D angle-interlock woven composites

Strengthening the Interface Between Individual Aramid Fibers and Polymer at Room and Elevated Temperatures

Effects of space environment temperature on the mechanical properties of carbon fiber/bismaleimide composites laminates