Microstructural evolution of external cold extrusion spinning 304 stainless steel with cumulative large deformation in multiple passes

Yiwei Xu,Weizhuang Li,Wang Tian,Jianguo Liang,Guoqing Zhang,Chunjiang Zhao

DOI: https://doi.org/10.1007/s00170-022-10107-4

2022-10-08

Abstract:In this paper, the strain-induced martensite transformation (SIMT) process of 304 stainless steel tubes under the action of a high shear stress state (HSSS) in the deformation zone of a new spinning process is studied and analyzes the changes in the microstructure and mechanical properties of each tubular workpiece obtained after continuous cold spinning under HSSS. Firstly, the contact equations and stress–strain state equations for the external cold extrusion spinning (ECES) were established and combined with the stress state criterion to find that ECES has a higher softening coefficient than conventional spinning (CS) in the deformation zone. To study the performance of the workpiece at each stage of processing, a longitudinal unidirectional tensile test was carried out on 304 stainless steel tubes. The material was obtained by cold spinning 5 times in succession for each pass of the tube, while X-ray diffraction (XRD) analysis was performed to measure the phase volume fraction of the workpiece at each stage, which provides a reference for subsequent transmission electron microscope (TEM) observation of the microstructure. The results show that the martensitic phase changes gradually after the volume fraction of martensite grows to a peak of 35% and gradually refines and fractures in tension, forming ultra-fine grain size laths of martensitic phase, while the tensile limit increases by 2.1 times, at which time the elongation at break is less than 5%.

engineering, manufacturing,automation & control systems