Thermal shock resistance and toughening mechanism of W/Ta and W/TiN/Ta laminated composites

Gaoyong Xu,Zizhi Yan,Hui Lu,Jili Cai,Ruoqi Wang,Fan Feng,Chao Cai,Jinping Suo

DOI: https://doi.org/10.1016/j.ijrmhm.2022.105810

IF: 4.804

2022-06-01

International Journal of Refractory Metals and Hard Materials

Abstract:The brittleness of tungsten (W) is a significant limitation on its widespread applications as a high-temperature structural material. Laminated composite technology proved to be an effective method to improve the toughness of W. In this work, W/Ta and W/TiN/Ta laminated composites were prepared by spark plasma sintering (SPS) to overcome the brittleness of W. The toughening properties of the W/Ta and W/TiN/Ta laminated composites were evaluated by electron beam thermal shock and laser thermal diffusivity testing. The toughening mechanism was clarified by scanning electron microscopy, electron probe micro-analysis, and transmission electron microscopy. After the three-point bending test, interfacial debonding was observed predominantly at the incoherent W-TiN rather than at the semi-coherent Ta-TiN interfaces. At 0.30 GW/m2 of electron beam thermal shock, the average width and depth of thermal shock cracks in the W/Ta laminated composite were ~ 9.4 μm and ~ 30.0 μm, respectively, which were much smaller than those in the W/W laminates and W/TiN/Ta laminated composite.

materials science, multidisciplinary,metallurgy & metallurgical engineering