Phase relations and extrinsic magnetic properties of Sm–(Fe,Co)–Ti–(Ga)-based alloys for ThMn12-type permanent magnets
A.K. Srinithi,H. Sepehri-Amin,Xin Tang,P. Tozman,J. Li,J. Zhang,S. Kobayashi,T. Ohkubo,T. Nakamura,K. Hono
DOI: https://doi.org/10.1016/j.jmmm.2021.167866
IF: 3.097
2021-07-01
Journal of Magnetism and Magnetic Materials
Abstract:<p>Realizing a non-ferromagnetic intergranular phase for the ThMn<sub>12</sub>-type Sm(Fe,Co,Ti)<sub>12</sub> compound is a prerequisite for developing high coercive magnets. In this work, we demonstrate that the addition of Ga into the Sm–(Fe,Co)–Ti system results in the formation of non-ferromagnetic Sm–Ga-rich intergranular phases with good wettability on Sm(Fe,Co,Ti)<sub>12</sub> grains. In the Sm-(Fe,Co)-Ti system, when the alloy composition was varied to the Sm-rich region as Sm<sub>1+</sub><em><sub>w</sub></em>(Fe<sub>0.8</sub>Co<sub>0.2</sub>)<sub>11</sub>Ti (<em>w</em>=0–0.7), soft ferromagnetic C15-type Sm(Fe,Co)<sub>2</sub> intergranular phase and TbCu<sub>7</sub>-type Sm(Fe,Co,Ti)<sub>∼7</sub> phase were formed in the as-cast alloy. We demonstrated that by introducing Ga, the formation of these secondary soft ferromagnetic phases can be hindered since the excess Sm and Ga formed non-ferromagnetic Ba<sub>5</sub>Si<sub>3</sub>-type Sm<sub>5</sub>Ga<sub>3</sub> and TII-type SmGa intergranular phases with an excellent wettability on Sm(Fe,Co,Ti)<sub>12</sub> grains. Fine Sm(Fe,Co,Ti)<sub>12</sub> grains of 1-2 µm, well isolated by the Sm–Ga-rich intergranular phase, were realized by melt-spinning the Ga-doped alloy and the maximum coercivity obtained was 0.5 T. According to the detailed microstructure characterizations, the weak-links to the coercivity of this novel microstructure of well-isolated and fine Sm(Fe,Co,Ti)<sub>12</sub>-based grains is the presence of defects at the interfaces which could lead to a locally reduced magneto-crystalline anisotropy.</p>
materials science, multidisciplinary,physics, condensed matter