High-coercivity SmFe 12 -based anisotropic sintered magnets by Cu addition

A.K. Srinithi,Xin Tang,H. Sepehri-Amin,J. Zhang,T. Ohkubo,K. Hono

DOI: https://doi.org/10.1016/j.actamat.2023.119111

IF: 9.4

2023-06-28

Acta Materialia

Abstract:We achieved a record-high coercivity of 1.40 T in a SmFe 12 -based ThMn 12 -type anisotropic sintered magnet. This magnet was prepared by sintering jet-milled powder made from strip-cast alloys with a nominal composition of Sm 8 Fe 73.5 Ti 8 V 8 Al 2 Cu 0.5 , using the conventional process for anisotropic sintered magnet production. Detailed microstructural investigations conducted using scanning electron microscopy and transmission electron microscopy revealed that the formation of Fe-lean intergranular phases (with < 20 at.% of Fe) surrounding the fine SmFe 12 phase grains resulted in the high coercivity. Nanobeam electron diffraction patterns showed that these Fe-lean intergranular phases (IGPs) exhibiting excellent wettability in this magnet are mainly composed of two phases: a hexagonal close-packed Mg-type Sm-based phase and a primitive cubic CsCl-type SmCu-based phase, which co-exist in the same intergranular region. Such Fe-lean IGPs minimize the intergranular exchange coupling in the SmFe 12 main phase, which contributes to the high coercivity, as revealed by magneto-optical Kerr effect microscopy. Overall, this study provides detailed microstructure-coercivity correlations and insights for the future development of high-performance SmFe 12 -based sintered magnets.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper aims to address the issue of high coercivity in samarium-iron (SmFe) based hard magnetic materials for practical applications. Specifically, the research team successfully prepared anisotropic sintered samarium-iron magnets with a record high coercivity (1.40 Tesla) by improving the processing methods and adding copper elements to the alloy. The main issues the paper attempts to solve are as follows:

1. **Increase Coercivity**:
- Samarium-iron based hard magnetic materials have been widely studied as candidate materials for permanent magnets due to their strong uniaxial magnetocrystalline anisotropy. However, their coercivity has not reached the level required for practical applications.
- Previous studies have shown that reducing the iron content in the grain boundary phase can effectively enhance coercivity. This paper significantly reduced the iron content in the grain boundary phase (<20 atomic percent) by adding copper elements, thereby greatly enhancing the coercivity.

2. **Optimize Microstructure**:
- The researchers used strip casting technology to prepare the powder and further prepared samarium-iron based magnets through a sintering process. Compared with traditional methods, this new processing method can obtain finer and more uniformly distributed grains.
- Microstructural analysis showed that the grain boundary phase formed after adding copper mainly consists of hexagonal close-packed magnesium-type samarium-based phase and simple cubic cesium chloride-type samarium-copper-based phase. These non-ferromagnetic grain boundary phases effectively weaken the exchange coupling between grains, thereby increasing the coercivity.

3. **Improve Thermal Stability**:
- The paper also explores the changes in coercivity of the magnets at different temperatures. The results show that the samarium-iron based magnets with added copper not only exhibit higher coercivity at room temperature but also have better thermal stability at high temperatures.

In summary, this study achieved a significant breakthrough in the coercivity of samarium-iron based magnets by improving the processing technology and adjusting the alloy composition. It provides important theoretical basis and technical support for the further development of high-performance samarium-iron based sintered magnets.