Abstract:The hot -dip 55 wt%Al-Zn-1.6 wt%Si-(0-3)wt.%Mg alloy coatings were experimentally investigated, and the solidification behaviors and hot cracking susceptibility were simulated by means of CALPHAD (CALculation of PHAse Diagrams) method. The scanning electron microscopy (SEM), electron probe micro -analyzer (EPMA) and glow discharge spectrometer method (GDS) were utilized to determine the microstructures and the distribution of elements of the Al-Zn-Mg alloy coatings with different Mg contents. It is discovered that with the increase of Mg content, the percentage of the eutectic microstructure scales up, and the surface quality of the alloy coating is improved. Meanwhile, the bending properties of Al-Zn-Mg coatings with different Mg contents still requires further improvement according to the present bending test. Subsequently, the equilibrium solidification processes of the coatings were calculated using thermodynamic approach. In general, the calculated results reflect the solidified phases and the precipitated temperatures according to theory of equilibrium solidification. However, there still exist discrepancies between the thermodynamic calculation results and the observed experimental results during the practical galvanizing process, because the cooling rates were not taken fully into consideration. Consequently, the kinetic analysis was carried out to obtain the secondary dendrite arm spacing under different cooling rates. The cracking susceptibility index (CSI) was also calculated to predict the hot workability of the Al-Zn-Mg alloy coating. In summary, the appropriate increase of the cooling rate turns out be the effective approach to benefit the microstructure and the corrosion resistance of the Al-Zn-Mg coatings in the practical galvanizing process, and the coating is not suitable for the hot stamping process.

In-situ localization of damage in a Zn-Al-Mg coating deposited on steel by continuous hot-dip galvanizing

In-situ localization of damage in a Zn-Al-Mg coating deposited on steel by continuous hot-dip galvanizing

Deformation and damage mechanisms of zinc coatings on hot-dip galvanized steel sheets: Part II. Damage modes

Microstructural factors controlling crack resistance of Zn–Al–Mg alloy coatings prepared via hot-dip galvanizing process: Combined approach of in-situ SEM observation with digital image correlation analysis

Experimental Investigation and Kinetic Analysis of Al–Zn–Mg Alloy Coating

Impact of Copper, Tin and Titanium Addition on Bending-Induced Damage of Intermetallic Phases in Hot Dip Galvanizing

Nanoscale Investigation of Microcracks and Grain Boundary Wetting in Press Hardened Galvanized 20MnB8 Steel

Microstructure of Hot-Dip Galvanized Zn-Al-Mg Alloy Coating

Impact of cooling rates on the microstructure and cracking susceptibility of hot-dip galvanized Zn-12 wt% Al-5 wt% Mg coatings

In-Situ Wettability Analysis of Al Coating Influence on Hot-Dip Galvanizing Properties of Advanced High-Strength Steels

In-situ investigation of damage mechanisms in duplex AlCoCrFeNi2.1 high entropy alloy

Characterization of hot-dip galvanized coating on dual phase steels

Experimental Investigation of Hot Forming of Zn‐Coated Hot‐Stamping Steel

Investigation of the LME Susceptibility of Dual Phase Steel with Different Zinc Coatings

Rate dependence of damage formation in metallic-intermetallic Mg-Al-Ca composites

Semi in-situ investigations on deformation-induced micro-damage in high-strength dual-phase steels

Roles of Al and Mg on the Microstructure and Corrosion Resistance of Zn-Al-Mg Hot-Dipped Coated Steel

Strain heterogeneity and micro-damage nucleation under tensile stresses in an Mg-5Al-3Ca alloy with an intermetallic skeleton

Corrosion mechanisms of Al‐alloyed hot‐dipped zinc coatings in wet supercritical carbon dioxide

Revisiting the Cracking of Chemical Conversion Coating on Magnesium Alloys

Grain size and orientation affected deformation inhomogeneity and local damage of hot-deformed Al-Zn-Mg alloy