Li 0.625 Al 0.125 H 0.25 Cl 0.75 O 0.25 Superionic Conductor with Disordered Rock-Salt Structure
Qian Zhang,William Arnold,Zachary D. Hood,Yang Li,Rachel DeWees,Miaofang Chi,Zhiwen Chen,Yan Chen,Hui Wang
DOI: https://doi.org/10.1021/acsaem.1c01011
IF: 6.4
2021-07-19
ACS Applied Energy Materials
Abstract:Solid-state Li-ion conductors are of broad interest in electrochemical energy storage, especially in solid-state Li batteries that serve as a promising alternative for the next-generation safe and high-energy-density batteries. Exploring solid-state superionic conductors is significant for the development of solid-state Li batteries with high performance. Herein, we report a disordered rock-salt (A<sub>1</sub>B<sub>1</sub>)-structured solid electrolyte (Li<sub>0.625</sub>Al<sub>0.125</sub>H<sub>0.25</sub>)(Cl<sub>0.75</sub>O<sub>0.25</sub>) (abbr. LAHCO) that was synthesized using Li<sub>2</sub>OHCl and LiAlCl<sub>4</sub> as precursors. Neutron diffraction reveals that Li, Al, and H atoms occupy the A sites and O and Cl atoms occupy the B sites in the A<sub>1</sub>B<sub>1</sub> structure for pure LAHCO. The LAHCO compound with excess LiAlCl<sub>4</sub> shows the highest Li<sup>+</sup> ionic conductivity of ∼10<sup>–4</sup> S cm<sup>–1</sup> at room temperature due to the disordering induced by configurational entropy as well as the entropy of mixing. Moreover, LAHCO–LiAlCl<sub>4</sub> solid electrolyte exhibits a stable polarization voltage under a current density of 5–50 μA cm<sup>–2</sup> in Li symmetric cells. This work not only explicates the importance of Li-ion conductors with a rock-salt structure but also contributes toward the development of solid-state Li-ion conductors for broad applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c01011?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c01011</a>.Neutron diffraction patterns of LiAlCl<sub>4</sub> precursor, (1 – <i>x</i>)Li<sub>2</sub>OHCl·<i>x</i>LiAlCl<sub>4</sub> series compounds (<i>x</i> = 0.4, 0.5, 0.6); XRD patterns of pure (Li<sub>0.625</sub>Al<sub>0.125</sub>H<sub>0.25</sub>)(Cl<sub>0.75</sub>O<sub>0.25</sub>) and LiCl and in situ XRD patterns of the 0.4Li<sub>2</sub>OHCl·0.6LiAlCl<sub>4</sub> sample; Nyquist plots of the 0.4Li<sub>2</sub>OHCl·0.6LiAlCl<sub>4</sub> sample under different temperatures and Nyquist plots of (1 – <i>x</i>)Li<sub>2</sub>OHCl·<i>x</i>LiAlCl<sub>4</sub> compounds (<i>x</i> = 0.33, 0.5, 0.6, 0.8, 1.0) at room temperature; and Arrhenius plots of 0.4Li<sub>2</sub>OHCl·0.6LiAlCl<sub>4</sub>, Li<sub>2</sub>OHCl, and LiCl (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c01011/suppl_file/ae1c01011_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels