Li_0.625Al_0.125H_0.25Cl_0.75O<s ub>0.25</sub> Superionic Conductor with Disordered Rock-Salt Structure

Qian Zhang,William Arnold,Zachary D. Hood,Yang Li,Rachel DeWees,Miaofang Chi,Zhiwen Chen,Yan Chen,Hui Wang

DOI: https://doi.org/10.1021/acsaem.1c01011

IF: 6.4

2021-01-01

ACS Applied Energy Materials

Abstract:Solid-state Li-ion conductors are of broad interest in electrochemical energy storage, especially in solid-state Li batteries that serve as a promising alternative for the next-generation safe and high-energy-density batteries. Exploring solid-state superionic conductors is significant for the development of solid-state Li batteries with high performance. Herein, we report a disordered rock-salt (A(1)B(1))-structured solid electrolyte (Li0.625Al0.125H0.25)(Cl0.75O0.25) (abbr. LAHCO) that was synthesized using Li2OHCl and LiAlCl4 as precursors. Neutron diffraction reveals that Li, Al, and H atoms occupy the A sites and O and Cl atoms occupy the B sites in the A(1)B(1) structure for pure LAHCO. The LAHCO compound with excess LiAlCl4 shows the highest Li+ ionic conductivity of similar to 10(-4) S cm(-1) at room temperature due to the disordering induced by configurational entropy as well as the entropy of mixing. Moreover, LAHCO-LiAlCl4 solid electrolyte exhibits a stable polarization voltage under a current density of 5-50 mu A cm(-2) in Li symmetric cells. This work not only explicates the importance of Li-ion conductors with a rock-salt structure but also contributes toward the development of solid-state Li-ion conductors for broad applications.