Development of large-volume $^{130}$TeO$_2$ bolometers for the CROSS $2β$ decay search experiment

F.T. Avignone III,A.S. Barabash,V. Berest,L. Bergé,J.M. Calvo-Mozota,P. Carniti,M. Chapellier,I. Dafinei,F.A. Danevich,L. Dumoulin,F. Ferella,F. Ferri,A. Gallas,A. Giuliani,C. Gotti,P. Gras,A. Ianni,L. Imbert,H. Khalife,V.V. Kobychev,S.I. Konovalov,P. Loaiza,P. de Marcillac,S. Marnieros,C.A. Marrache-Kikuchi,M. Martinez,S. Nisi,C. Nones,E. Olivieri,A. Ortiz de Solórzano,Y. Peinaud,G. Pessina,D.V. Poda,Ph. Rosier,J.A. Scarpaci,V.I. Tretyak,V.I. Umatov,M.M. Zarytskyy,A. Zolotarova
2024-07-24
Abstract:We report on the development of thermal detectors based on large-size tellurium dioxide crystals (45x45x45 mm), containing tellurium enriched in $^{130}$Te to about 91%, for the CROSS double-beta decay experiment. A powder used for the crystals growth was additionally purified by the directional solidification method, resulting in the reduction of the concentration of impurities by a factor 10, to a few ppm of the total concentration of residual elements (the main impurity is Fe). The purest part of the ingot (the first ~200 mm, about 80% of the total length of the cylindrical part of the ingot) was determined by scanning segregation profiles of impurities and used for the $^{130}$TeO$_2$ powder production with no evidence of re-contamination. The crystal growth was verified with precursors produced from powder with natural Te isotopic composition, and two small-size (20x20x10 mm) samples were tested at a sea-level laboratory showing high bolometric and spectrometric performance together with acceptable $^{210}$Po content (below 10 mBq/kg). This growth method was then applied for the production of six large cubic $^{130}$TeO$_2$ crystals and 4 of them were taken randomly to be characterized at the Canfranc underground laboratory, in the CROSS-dedicated low-background cryogenic facility. Two $^{130}$TeO$_2$ samples were coated with a thin, $O$(100 nm), metal film in form of Al layer (on 4 sides) or AlPd grid (on a single side) to investigate the possibility to tag surface events by pulse-shape discrimination. Similarly to the small natural precursors, large-volume $^{130}$TeO$_2$ bolometers show high performance and even better internal purity ($^{210}$Po activity $\sim$ 1 mBq/kg, while activities of $^{228}$Th and $^{226}$Ra are below 0.01 mBq/kg), satisfying requirements for the CROSS and, potentially, next-generation experiments.
Instrumentation and Detectors,Nuclear Experiment
What problem does this paper attempt to address?