Identification and characterization of three-dimensional crack propagation mechanism in the Aluminium alloy AA2024-T3 using high-resolution Digital Image Correlation

Vanessa Schöne,Florian Paysan,Eric Breitbarth

2024-04-02

Abstract:Fatigue crack growth is usually a three-dimensional problem, but it is often simplified to two dimensions to reduce complexity. However, this study investigates the relationships between microscopic effects such as crack kinking, shear lips, and plasticity that are present in reality. Therefore, crack propagation tests were carried out on 2-mm-thick MT-160 specimens of AA2024-T3 sheet material in L-T and T-L orientation. Using high-resolution digital image correlation (DIC), the plastic zone was identified and measured on the samples surface. The fracture surfaces were then digitized and their 3D shape characterized. Finite element simulations confirm the presence of a local mixed-mode I/II/III state along the crack front for a slant or double shear-fracture type. A derived mapping function enables the determination of the fracture type from the surface plastic zone, along with the current crack tip loading during the test. Finally, a transition of the fracture type also leads to a short-term delay in the crack propagation rate. Based on this information crack propagation curves are computed with regards to the local 3D crack orientation.

Materials Science

What problem does this paper attempt to address?

The problem this paper attempts to address is:

Fatigue crack growth is typically a three-dimensional problem, but in practical applications, it is often simplified to a two-dimensional problem to reduce complexity. However, this simplification overlooks the effects of micro-scale phenomena such as crack deflection, shear lips, and plasticity. Therefore, this paper investigates the three-dimensional crack growth mechanisms of AA2024-T3 aluminum alloy in the L-T and T-L directions using high-resolution digital image correlation (HR-DIC) technology. Specifically, this paper aims to:

1. **Identify and characterize the plastic zone during the crack growth process**: Identify and measure the plastic zone on the specimen surface using HR-DIC technology.
2. **Analyze the three-dimensional shape of the crack surface**: Digitize the crack surface using an optical 3D scanner and characterize its three-dimensional shape.
3. **Validate finite element simulation results**: Confirm the presence of local mixed-mode I/II/III states at the crack front through finite element simulations, especially in inclined or double shear fracture types.
4. **Establish a mapping function**: Determine the fracture type and the loading conditions at the crack tip during testing through the surface plastic zone.
5. **Study the variation in crack growth rate**: Based on the above information, calculate the da/dN−∆Keqv curve considering the local three-dimensional crack orientation and explore the short-term delay effect of fracture type changes on the crack growth rate.

Through these studies, the authors hope to more accurately describe and predict the three-dimensional growth behavior of fatigue cracks, thereby improving the life prediction of structural components and enhancing the resource utilization efficiency of materials.