Abstract:Four molecular dynamics models of nanocrystalline Al with different grain boundary (GB) contents are established. The results show that the high‐content GBs in polycrystals increase the toughness, reducing the risk of brittle crack propagation. High‐content GBs can induce a more even deformation and actuate more plastic deformation mechanisms such as multiple slips, GB slip, and migration.The nanocrystalline metal material has been an investigation hotspot due to its excellent mechanical property. The high content of grain boundaries (GBs) in microstructure is the key factor affecting its fracture behavior during service. Therefore, it is essential to investigate the effect mechanism of nanoscale GB on crack propagation. In this study, four molecular dynamics (MD) models of nanocrystalline aluminum (Al) with different GB contents are established. The results show that the high‐content GBs in polycrystals can increase the toughness and absorb energy, reducing the risk of brittle crack propagation. The presence of GB can reduce the stress concentration of the crack, and the dislocation emission from the crack tip can be absorbed by the front GB. The microstructure with high‐content GBs can actuate more plastic deformation mechanisms such as multiple slips, GB slip, and migration. The region with more GBs can induce a more even deformation of the whole microstructure by means of dislocation emission and GB migration to the region with fewer GBs. The purpose of this study is to provide a rational mechanism reference for the failure of nanocrystalline metal material.

Molecular Dynamics Simulation of the Interaction between Cracks in Single-Crystal Aluminum

Molecular Dynamics Simulations of Pre-Crack Effects on Deformation and Failure Mechanisms for Pure Aluminum

Molecular dynamics simulation of grain boundary geometry on crack propagation of bi-crystal aluminum

Dynamics of nanoscale grain-boundary decohesion in aluminum by molecular-dynamics simulation

Molecular dynamics simulation of fracture in α-iron

Cracking in a Fe–25Mn–3Si–3Al Steel

Molecular dynamics simulation of the mechanical behavior of bi-crystal interfaces

Microscopic and macroscopic analyses of the interaction mechanism between defect growth and dislocation emission in single‐crystal aluminum

The effect of constant electric field on the crack growth process of aluminum nanosheet using molecular dynamics simulation

Molecular dynamics simulation of crack propagation behaviors at the Ni/Ni3Al grain boundary

Investigation of Grain Boundary Content on Crack Propagation Behavior of Nanocrystalline Al by Molecular Dynamics Simulation

Molecular dynamics simulation on plastic deformation and failure mechanisms around a crack tip for magnesium alloys

Mechanical behavior and microstructure evolution of Al/AlCu alloy interface

Three-dimensional Quantitative in Situ Study of Crack Initiation and Propagation in AA 6061 Aluminum Alloy Sheets Via Synchrotron Laminography and Finite-Element Simulations

Molecular dynamics simulation of effects of loading parameters on fatigue crack growth behavior in titanium single crystal

Fracture Behavior of Functionally Graded Joint Interfaces Between Copper and Aluminum at Nano-Scale

Dislocation formation and twinning from the crack tip in Ni_3Al:molecular dynamics simulations

Dislocation formation and twinning from the crack tip in Ni 3 Al: molecular dynamics simulations

Molecular Dynamics Study on Interaction Between Voids for Pure Aluminum

Multi-scale numerical simulation of fracture behavior of nickel-aluminum alloy by coupled molecular dynamics and cohesive finite element method (CFEM)

Molecular Dynamics Simulation on Crack Propagation for Magnesium