Effect of annealing on the hot salt corrosion resistance of the fine-grained titanium alpha-alloy Ti-2.5Al-2.6Zr obtained via cold Rotary Swaging

V. N. Chuvil'deev,A. V. Nokhrin,C. V. Likhnitskii,A. A. Murashov,N. V. Melekhin,K. A. Rubtsova,A. M. Bakmetyev,P. V. Tryaev,R. A. Vlasov,N. Yu. Tabachkova,A. I. Malkin

2024-03-20

Abstract:A hot salt corrosion (HSC) test was performed on the fine-grained titanium alpha-alloy Ti-2.5Al-2.6Zr (Russian industrial alloy PT-7M). The ultrafine-grained (UFG) microstructure in the titanium alpha-alloy was formed via cold Rotary Swaging. The grain size and volume fraction of the recrystallized microstructure in the alloy were varied by choosing appropriate annealing temperatures and times. The microstructure and corrosion resistance of UFG alloys were studied after 30 min of annealing at 500-700C and after 1000 h of annealing at 250C. Metallographic studies were carried out to investigate the effects of annealing on the nature and extent of corrosive damage in the titanium alpha-alloy Ti-2.5Al-2.6Zr. After HSC tests, surface analyses of the titanium alpha-alloy samples were conducted using X-ray diffraction and electron microscopy. During the HSC testing of the titanium alpha-alloy Ti-2.5Al-2.6Zr, a competitive interaction between intergranular corrosion (IGC) and pitting corrosion was observed. To the best of our knowledge, it was shown for the first time that annealing affects the relationship among the IGC, pitting corrosion and uniform corrosion rates of the titanium alloy. Prolonged low-temperature annealing at 250C resulted in a more pronounced increase in the uniform corrosion rate than short-term high-temperature annealing for 30 min at 500-700C. An in-depth analysis of the effect of the structure and phase composition of the grain boundaries on the susceptibility of the alpha-alloy Ti-2.5Al-2.6Zr to HSC was conducted.

Applied Physics,Materials Science

What problem does this paper attempt to address?

The paper aims to study the high-temperature salt corrosion (HSC) behavior and the effects of microstructural changes of fine-grained titanium α-alloy Ti–2.5Al–2.6Zr under different annealing conditions. Specifically:

1. **Research Background**: Titanium α-alloys are widely used in nuclear engineering and marine aviation due to their excellent corrosion resistance. However, high-temperature salt corrosion is a critical issue, especially in the presence of oxygen and water vapor, leading to intergranular corrosion (IGC) and pitting corrosion.

2. **Research Objective**: To prepare ultrafine-grained (UFG) structure Ti–2.5Al–2.6Zr alloy using rotary swaging (RS) technology and to study the effects of different annealing temperatures and times on the alloy's microstructure and corrosion behavior. The focus is on exploring how the annealing process affects grain boundary migration and the changes in recrystallization volume fraction, and evaluating the impact of these changes on the HSC mechanism.

3. **Main Findings**:
- Short-term high-temperature annealing (30 minutes at 500-700°C) leads to grain growth and grain boundary migration, thereby affecting the rates of IGC and pitting corrosion.
- Long-term low-temperature annealing (1000 hours at 250°C) results in a significant increase in uniform corrosion rate.
- Changes in the structure and phase composition of grain boundaries during annealing have a significant impact on the alloy's HSC sensitivity.

In summary, this study systematically explores the effects of annealing processes on the high-temperature salt corrosion behavior of fine-grained titanium alloys through experimental and analytical methods, providing theoretical basis and technical support for further optimization of the corrosion resistance of titanium alloys.