Abstract:Mechanical behaviors of a Ni-based single crystal superalloy have been investigated by tensile testing at various temperatures. Deformation substructures and mechanisms have been systemically revealed from micrometer to atomic scales by using advanced scanning electron and scanning transmission electron microscopes. Results show that deformation mode of the alloy strongly depends on the temperature due to competitive responses of the gamma and gamma' phases under mechanical loading and their original stress statuses. At temperatures from ambient to 750 degrees C, plasticity is governed by dislocation shearing in both phases, where slip modes of gamma are < 110 >{111} and those of gamma' are < 112 >{111}, < 110 >{111} and < 110 > {001}. At moderate temperatures (850 degrees C <= T <= 900 degrees C), plasticity mainly involves microscopically uniform deformation of both phases. The matrix deforms first so that channels parallel to tensile direction are narrowed due to the Poisson's effect, after that deformation of gamma' follows. The active slip modes are < 110 > {111} for gamma, < 112 >{111}, < 110 >{111}, < 110 >{001}, and < 001 >{001} for gamma'. At temperature higher than 1000 degrees C, plastic strain is also derived from deformation of both phases, but deformation of the matrix plays critical roles, due to relatively weak strength of this phase. The operative slip modes are < 110 > {111} for gamma, but mainly < 110 >{001} and < 001 >{001} for gamma'. Our results clearly provide a comprehensive and multiscale (from micrometer to atomic) understanding on the deformation mechanism of Ni-based superalloys, which can be critically beneficial and offer mechanistic guidelines to design new/next generation superalloys. (c) 2021 Elsevier Ltd. All rights reserved.

$α$-Al$_2$O$_3$ sapphire and rubies deformed by dual basal slip at intermediate temperatures (900C-1300$^\circ$C) -- II. dissociation and stacking faults

Chromium hardening and Peierls mechanism for basal slip in sapphire at temperatures between 900 and 1500 $^\circ$C

Analysis of a kink pair model applied to a peierls mechanism in basal and prism plane slips in sapphire deformed between 200C and 1800C

Shearing Mechanisms of Stacking Fault and Anti-Phase-boundary Forming Dislocation Pairs in the Γ′ Phase in Ni-based Single Crystal Superalloy

The Core Structure of Basal Dislocations in Deformed Sapphire (Α-Al 2 O 3 )

The Core Structure of Basal Dislocations in Deformed Sapphire (α-Al2O3)

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

On the temperature and chemical dependency of prismatic stacking faults in C14 Laves phases

Superlattice Dislocations in Ti-rich Polysynthetically Twinned Crystals of TiAl

A continuum description of nonlinear elasticity, slip and twinning, with application to sapphire

Nanoscale Stacking Fault–assisted Room Temperature Plasticity in Flash-Sintered TiO2

Uncovering the crystal defects within aragonite CaCO3

Deformation mechanisms of basal slip, twinning and non-basal slips in Mg–Y alloy by micropillar compression

Stacking faults and the γ-surface on {1-101} pyramidal planes in α-titanium

Role of stacking defects on the magnetic behavior of CrCl$_3$

Concentration-Dependent High-Temperature Deformation Mechanism of Hexagonal Close-Packed Ti-Al Alloys

Cyclic deformation behavior and dislocation structure of Ti-2 at. Pct Al single crystals oriented for double prism slip

Mechanisms of cyclic deformation of NiAl single crystals at high temperatures

Investigation of Tensile Deformation Mechanisms at Room Temperature in A New Ni-Based Single Crystal Superalloy

The Role of < 112 > {111} Slip in the Initial Plastic Deformation of Ni-base Superalloys at Room Temperature

Bonding Layer Microstructures and Mechanical Behavior of Sapphire/Sapphire Joints Diffusion-Bonded Using Mgo-Al2o3-Sio2 Interlayer