Abstract:Plastic deformation of the brittle C14-Fe$_2$Nb Laves phase occurs mostly by basal slip due to the complex crystal structure. Here, we compare the barriers for basal slip for the known mechanisms of direct slip, synchroshear and undulating slip using density functional theory calculations. According to our calculated generalized stacking fault (SF) energies, the most favorable mechanisms are synchroshear and undulating slip. Both mechanisms lead to stable SF with a formation energy of 50 $mJ/m^2$ through the same unstable SF configuration at the transition. The energy barrier of approximately 3 $J/m^2$ indicates a low dislocation mobility as expected from the brittle character. We also determine the influence of vacancies and antisite defects on the formation energy of stable and unstable SF. Both kinds of point defects tend to lower the energy barrier on both sides of 2:1 stoichiometry. This explains the experimentally observed off-stoichiometric softening of C14-Fe$_2$Nb. The small energy differences between the Fe$_2$Nb Laves phase polytypes raises the question if there are further deformation mechanisms with low barrier. Therefore, we additionally consider transformations between C14, C15 and C36 Laves phases as further deformation mechanism. Our calculations for polytypic transformations by successive synchroshear steps show that the corresponding energy barriers are in fact very similar to the energy barrier for basal slip in C14. This suggests that the energy needed to create a stable SF in C14 by synchroshear is also sufficient to initiate polytypic transformations where existing SFs in C14 are further transformed to form C15 or C36 Laves phases.

On the temperature and chemical dependency of prismatic stacking faults in C14 Laves phases

Local Lattice Distortion Mediated Formation of Stacking Faults in Mg Alloys

Shearing Mechanisms of Stacking Fault and Anti-Phase-boundary Forming Dislocation Pairs in the Γ′ Phase in Ni-based Single Crystal Superalloy

Basal Planar Fault Formation in a Chemically Complex Laves Phase Containing Eutectic High Entropy Alloy

Undulating Slip In Laves Phase And Implications For Deformation In Brittle Materials

Ab Initio Study of Stacking Faults and Deformation Mechanism in C15 Laves Phases Cr2x (X = Nb, Zr, Hf)

Ab initio study of I 2 and T 2 stacking faults in C14 Laves phase MgZn 2

Shuffle and glide mechanisms of prismatic dislocations in a hexagonal C 14 -type Laves-phase intermetallic compound

Self-accommodated defect structures modifying the growth of Laves phase

Shuffle and Glide Mechanisms of Prismatic Dislocations in a Hexagonal C14 -Type Laves-phase Intermetallic Compound

Off-stoichiometric softening and polytypic transformations in the plastic deformation of the C14 Fe$_2$Nb Laves phase

The formation mechanism of stacking faults in ZrFe2 Laves phase in Zircaloy-4 alloy

Revealing Complex Planar Defects and Their Interactions at Atomic Resolution in a Laves Phase Containing Co-base Superalloy

Influence of chemical composition on the room temperature plas-ticity of C15 Ca-Al-Mg Laves phases

The Formation and Destruction of Stacking Fault Tetrahedron in Fcc Metals: A Molecular Dynamics Study

Contribution of Van Der Waals Forces to the Plasticity of Magnesium

Unexpected {0111} pyramidal stacking faults in Zr(Fe, Cr)2 secondary phase particle induced by the C15C14 Laves phase transformation in Zircaloy-4

Unexpected {011¯1} pyramidal stacking faults in Zr(Fe, Cr)2 secondary phase particle induced by the C15→C14 Laves phase transformation in Zircaloy-4

Unexpected { 01 1 ̄ 1 } pyramidal stacking faults in Zr(Fe, Cr)2 secondary phase particle induced by the C15→C14 Laves phase transformation in Zircaloy-4

Stress-dependent Dislocation Core Structures Leading to Non-Schmid Behavior

Activation of pyramidal II slips at room temperature in Mg–Zn–Y 18R and 14H long-period stacking ordered phases