Abstract:This comprehensive study, being part of the European XFEL R\&D effort, elucidates the influence of medium temperature (mid-T) heat treatments between 250°C and 350°C on the performance of 1.3~GHz superconducting radiofrequency (SRF) niobium cavities. Utilizing a refurbished niobium retort furnace equipped with an inter-vacuum chamber and cryopumps at DESY, we have embarked on an investigation to enhance the state-of-the-art SRF cavity technology. Our research reveals that mid-T heat treatments significantly boost the quality factor ($Q_0$) of the cavities, achieving values between $2\cdot10^{10}$ to $5\cdot10^{10}$ at field strengths around 16~MV/m, while the maximum field strengths are limited to 25-35~MV/m and enhanced sensitivity to trapped magnetic flux is observed. Moreover, we delve into the effects of surface impurity concentration changes, particularly the diffusion of oxygen content, and its impact on performance enhancements. By categorizing treatments based on calculated diffusion lengths using the whole temperature profile, we recognize patterns that suggest an optimal diffusion length conducive to optimizing cavity performance. SIMS results from samples confirm the calculated oxygen diffusion lengths in most instances. Deviations are primarily attributed to grain boundaries in fine-grain materials, necessitating repeated measurements on single-crystal materials to further investigate this phenomenon. Investigations into cooling rates and the resulting spatial temperature gradients across the cavities ranging from 0.04 to 0.2~K/mm reveal no significant correlation with performance following a mid-T heat treatment. However, the increased sensitivity to trapped magnetic flux leads to new challenges in the quest for next-generation accelerator technologies since the requirement for magnetic hygiene gets stricter.

Medium-temperature furnace bake of Superconducting Radio-Frequency cavities at IHEP

Medium-temperature furnace baking of 1.3 GHz 9-cell superconducting cavities at IHEP

Effective medium temperature baking of 1.3 GHz single cell SRF cavities

Influence of Furnace Baking on Q-E Behavior of Superconducting Accelerating Cavities

Mid-T Heat Treatments on BCPed Coaxial Cavities at TRIUMF

Further improvement of medium temperature heat treated SRF cavities for high gradients

Advanced surface treatments for medium-velocity superconducting RF cavities for high accelerating gradient continuous-wave operation

High Q and high gradient performance of the first medium-temperature baking 1.3 GHz cryomodule

A Nearly Zero Temperature Gradient Furnace System for High Pressure Multi-Anvil Experiments

China’s Technological Achievements on ITER Enhanced Heat Flux First Wall in the Pre-Pa Qualification

Low-Temperature Baking Effect of the Radio-Frequency Nb<sub>3</sub>Sn Thin Film Superconducting Cavity

Effect of high temperature heat treatments on the quality factor of a large-grain superconducting radio-frequency niobium cavity

High and high gradient performance of the first medium-temperature baking 1.3 GHz cryomodule

Correlation of srf performance to oxygen diffusion length of medium temperature heat treated cavities

Ultra-Low Surface Resistance via Vacuum Heat Treatment of Superconducting Radiofrequency Cavities

A Path to Higher Q0 with Large Grain Niobium Cavities

Study on the interstitial oxygen diffusion to understand the reduction of cryogenic RF loss for the superconducting radio-frequency niobium cavities

Successful Nitrogen Doping of 1.3GHz Single Cell Superconducting Radio-Frequency Cavities

Researches On Bake Effect On Rf Superconducting Cavities

Continuous Wave Mode Test of Conduction-Cooled Nb3Sn Radio Frequency Superconducting Cavities at Peking University

Researches on Large Grain SC Cavities at Peking University