Abstract:We investigate the rf performance of several single-cell superconducting radio-frequency cavities subjected to low temperature heat treatment in nitrogen environment. The cavities were treated at temperature 120–165 °C for an extended period of time (24–48 h) either in high vacuum or in a low partial pressure of ultrapure nitrogen. The improvement in Q0 with a Q rise was observed when nitrogen gas was injected at ∼300 °C during the cavity cooldown from 800 °C and held at 165 °C , without any degradation in accelerating gradient over the baseline performance. The treatment was applied to several elliptical cavities with frequency ranging from 0.75 to 3.0 GHz, showing an improved quality factor as a result of low temperature nitrogen treatments. The Q rise feature is similar to that achieved by nitrogen alloying Nb cavities at higher temperature, followed by material removal by electropolishing. The surface modification was confirmed by the change in electronic mean free path and tuned with the temperature and duration of heat treatment. The decrease of the temperature-dependent surface resistance with increasing rf field, resulting in a Q rise, becomes stronger with increasing frequency and decreasing temperature. The data suggest a crossover frequency of ∼0.95 GHz above that the Q rise phenomenon occurs at 2 K. Some of these results can be explained qualitatively with an existing model of intrinsic field-dependence of the surface resistance with both equilibrium and nonequilibrium quasiparticle distribution functions. The change in the Q slope below 0.95 GHz may result from masking contribution of trapped magnetic flux to the residual surface resistance. https://doi.org/10.1103/PhysRevAccelBeams.27.062001 Published by the American Physical Society under the terms of the Creative Commons Attribution 4.0 International license. Further distribution of this work must maintain attribution to the author(s) and the published article's title, journal citation, and DOI. Published by the American Physical Society

Successful Nitrogen Doping of 1.3GHz Single Cell Superconducting Radio-Frequency Cavities

Effective medium temperature baking of 1.3 GHz single cell SRF cavities

The effect of nitrogen infusion on a 162.5 MHz low beta superconducting HWR cavity

Nitrogen and argon doping of niobium for superconducting radio frequency cavities: a pathway to highly efficient accelerating structures

Understanding the Mechanism of the Performance Improvement in Nitrogen-doped Niobium Superconducting Radio Frequency Cavity

Unraveling the Nanoscale Segregation Mechanism in N-Doped Niobium for Enhanced SRF Performance

Q-factor optimization for high-beta 650 MHz cavities for PIP-II

Nitrogen Doping/infusion of 650 MHz Cavities for CEPC

Advanced surface treatments for medium-velocity superconducting RF cavities for high accelerating gradient continuous-wave operation

Feasibility Study on SRF Cavity Improvement by Doping Method

Unprecedented Quality Factors at Accelerating Gradients up to 45 MV/m in Niobium Superconducting Resonators via Low Temperature Nitrogen Infusion

Field, frequency and temperature dependence of the surface resistance of nitrogen diffused niobium superconducting radio frequency cavities

Insight into bulk niobium superconducting RF cavities performances by tunneling spectroscopy

Improving the Stability of Pulse Superconducting Radio Frequency Cavities by the Construction of an Al-Nb Double Layer Structure

A Path to Higher Q0 with Large Grain Niobium Cavities

Low-Temperature Baking Effect of the Radio-Frequency Nb<sub>3</sub>Sn Thin Film Superconducting Cavity

XPS studies of nitrogen doping niobium used for accelerator applications

Field, frequency, and temperature dependencies of the surface resistance of nitrogen diffused niobium superconducting radio frequency cavities

Magnetic Properties and Hydrides Precipitation Observation of Nitrogen Doping Niobium Used for Accelerator Applications

Enhancement in Quality Factor of SRF Niobium Cavities by Material Diffusion

Advancement in the understanding of the field and frequency dependent microwave surface resistance of niobium