Abstract:This comprehensive study, being part of the European XFEL R\&D effort, elucidates the influence of medium temperature (mid-T) heat treatments between 250°C and 350°C on the performance of 1.3~GHz superconducting radiofrequency (SRF) niobium cavities. Utilizing a refurbished niobium retort furnace equipped with an inter-vacuum chamber and cryopumps at DESY, we have embarked on an investigation to enhance the state-of-the-art SRF cavity technology. Our research reveals that mid-T heat treatments significantly boost the quality factor ($Q_0$) of the cavities, achieving values between $2\cdot10^{10}$ to $5\cdot10^{10}$ at field strengths around 16~MV/m, while the maximum field strengths are limited to 25-35~MV/m and enhanced sensitivity to trapped magnetic flux is observed. Moreover, we delve into the effects of surface impurity concentration changes, particularly the diffusion of oxygen content, and its impact on performance enhancements. By categorizing treatments based on calculated diffusion lengths using the whole temperature profile, we recognize patterns that suggest an optimal diffusion length conducive to optimizing cavity performance. SIMS results from samples confirm the calculated oxygen diffusion lengths in most instances. Deviations are primarily attributed to grain boundaries in fine-grain materials, necessitating repeated measurements on single-crystal materials to further investigate this phenomenon. Investigations into cooling rates and the resulting spatial temperature gradients across the cavities ranging from 0.04 to 0.2~K/mm reveal no significant correlation with performance following a mid-T heat treatment. However, the increased sensitivity to trapped magnetic flux leads to new challenges in the quest for next-generation accelerator technologies since the requirement for magnetic hygiene gets stricter.

Researches On Bake Effect On Rf Superconducting Cavities

Influence of Furnace Baking on Q-E Behavior of Superconducting Accelerating Cavities

Effective medium temperature baking of 1.3 GHz single cell SRF cavities

Recent Progresses on RF Superconductivity

Low-Temperature Baking Effect of the Radio-Frequency Nb<sub>3</sub>Sn Thin Film Superconducting Cavity

Medium-temperature furnace baking of 1.3 GHz 9-cell superconducting cavities at IHEP

Further improvement of medium temperature heat treated SRF cavities for high gradients

Exploration of Parameters That Affect High Field Q-Slope

Advanced surface treatments for medium-velocity superconducting RF cavities for high accelerating gradient continuous-wave operation

Medium-temperature furnace bake of Superconducting Radio-Frequency cavities at IHEP

Ultra-Low Surface Resistance via Vacuum Heat Treatment of Superconducting Radiofrequency Cavities

Study on the interstitial oxygen diffusion to understand the reduction of cryogenic RF loss for the superconducting radio-frequency niobium cavities

Analysis of post wet chemistry heat treatment effects on Nb SRF surface resistance

Mid-T Heat Treatments on BCPed Coaxial Cavities at TRIUMF

Surface Resistance Effects of Medium Temperature Baking of Buffered Chemical Polished 1.3 GHz Nine-Cell Large-Grain Cavities

Researches On The Electromagnetic Field In Rf Superconducting Cavities

Researches on Large Grain SC Cavities at Peking University

Role of thermal resistance on the performance of superconducting radio frequency cavities

Correlation of srf performance to oxygen diffusion length of medium temperature heat treated cavities

New Results of Development on High Efficiency High Gradient Superconducting RF Cavities

Effect of high temperature heat treatments on the quality factor of a large-grain superconducting radio-frequency niobium cavity