Electrochemical characterization of RuO2-Ta2O5/polyaniline composites as potential redox electrodes for supercapacitors and hydrogen evolution reaction

Chung-Wen Kuo,Jui-Cheng Chang,Bo-Wei Wu,Tzi-Yi Wu
DOI: https://doi.org/10.1016/j.ijhydene.2019.08.059
IF: 7.2
2020-08-01
International Journal of Hydrogen Energy
Abstract:<p>RuO<sub>2</sub>-Ta<sub>2</sub>O<sub>5</sub> electrode covered with polyaniline (PANI) was prepared by sintering and electrodeposition. X-ray photoelectron spectroscopy confirmed the presence of RuO<sub>2</sub>-Ta<sub>2</sub>O<sub>5</sub> and PANI and the strong interaction between RuO<sub>2</sub>-Ta<sub>2</sub>O<sub>5</sub> and PANI in the RuO<sub>2</sub>-Ta<sub>2</sub>O<sub>5</sub>/PANI composite. The crystalline structure of RuO<sub>2</sub>-Ta<sub>2</sub>O<sub>5</sub>/PANI was verified by XRD. SEM analysis revealed that the RuO<sub>2</sub>-Ta<sub>2</sub>O<sub>5</sub>/PANI electrode had a nano-fibrous morphology with a crystal plane and some pores. The supercapacitive performance of RuO<sub>2</sub>-Ta<sub>2</sub>O<sub>5</sub>/PANI was evaluated by cyclic voltammetry and charge-discharge chronopotentiometry. RuO<sub>2</sub>-Ta<sub>2</sub>O<sub>5</sub>/PANI had a high specific capacitance (428 F/g), specific energy (26.7 Wh/kg at a discharge current density of 0.5 mA/cm<sup>2</sup>), and power density (2.4 kW/kg at a discharge current density of 4.0 mA/cm<sup>2</sup>). The attractive capacitive properties of RuO<sub>2</sub>-Ta<sub>2</sub>O<sub>5</sub>/PANI may be attributed to the porous morphology of RuO<sub>2</sub>-Ta<sub>2</sub>O<sub>5</sub> covered with PANI. In addition, the as-prepared RuO<sub>2</sub>-Ta<sub>2</sub>O<sub>5</sub> and RuO<sub>2</sub>-Ta<sub>2</sub>O<sub>5</sub>/PANI electrodes had Tafel slopes of −55.8 and −69.2 mV/dec, respectively, which make them potential H<sub>2</sub> evolution electrocatalysts.</p>
energy & fuels,electrochemistry,chemistry, physical
What problem does this paper attempt to address?