Abstract:Facile one‐step electrochemical polymerization of a novel graphitic oxide/polypyrrole/2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid composite on carbon fabric was developed for supercapacitor applications. In the aqueous electrolyte, the operating voltage reached 2.2 V, resulting in high‐energy density, power efficiency, and long cyclic capacity. Summary Facile one‐step electrochemical synthesis of a novel graphitic oxide/polypyrrole/2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid composite on carbon fabric were described for development of an efficient positive electrode for supercapacitor applications. The 2‐acrylamido‐2‐methyl‐1‐propanesulfonate monomers behave as dopant in 3D polypyrrole network formed by synergetic coupling with graphitic oxide. Their free acrylic groups interact with each other to form polymer‐hydrogel‐layer on the external surface that facilitate transport of aqueous electrolyte ions inside of the electrode. The most efficient electrode material was synthesized by tuning dopant concentration at 0.01 M. The full‐cell assembled using the composite electrode and graphite counter electrode works at 2.2 V in 3 M NaCl solution that equals to the highest values achieved yet for aqueous supercapacitors. This cell has a capacitance as high as 698.8 F g−1 at 5 mV s−1 and preserves its initial value even after 10 000 continuous CV cycles at 1000 mV s−1. It also exhibits a high‐energy density of 446.1 W h kg−1 at a power density of 366.7 W kg−1, and it is still 65.2 W h kg−1 at 18.3 kW kg−1. The asymmetric capacitor with 1 × 1 cm2 area successfully lit a red light‐emitting diode.

Fibriform Polyaniline/nano-Tio2 Composite As an Electrode Material for Aqueous Redox Supercapacitors

Tin Disulphide/nitrogen-Doped Reduced Graphene Oxide/polyaniline Ternary Nanocomposites with Ultra-High Capacitance Properties for High Rate Performance Supercapacitor.

Polyaniline Nanowire Array Encapsulated in Titania Nanotubes As a Superior Electrode for Supercapacitors

Synthesis and Properties of Poly(2,2'-Dithiodianiline-co-aniline)-graphene Oxide Nanocomposite As Electrode Material for Supercapacitors

AQUEOUS DISPERSED POLYANILINE NANO WIRES FOR ELECTRODE MATERIAL OF SUPERCAPACITOR

Nanostructured Palygorskite Modified Polyaniline Electrode Materials for Supercapacitors

In situ synthesis of polyaniline/sodium carboxymethyl cellulose nanorods for high-performance redox supercapacitors

Composites Based on Polyaniline and Activated IR-Pyrolyzed Polyacrylonitrile As Promising Supercapacitor Electrode Materials

Semi-Polycrystalline Polyaniline-Activated Carbon Composite for Supercapacitor Application

A Facilely Prepared Polypyrrole–reduced Graphene Oxide Composite with a Crumpled Surface for High Performance Supercapacitor Electrodes

Ag3O4 embedded fibre reinforced polyaniline nanocomposite as an electrode material for supercapacitors

Recycled Carbon Fiber-Supported Polyaniline/Manganese Dioxide Prepared via One-Step Electrodeposition for Flexible Supercapacitor Integrated Electrodes

Facile Synthesis and Electrochemical Characterization of Polyaniline@TiO2-CuO Ternary Composite as Electrodes for Supercapacitor Applications

Electrochemical synthesis of tunable polypyrrole‐based composites on carbon fabric for wide potential window aqueous supercapacitor

Design and synthesis of ternary composite of polyaniline-sulfonated graphene oxide-TiO2 nanorods: a highly stable electrode material for supercapacitor

Polyaniline-Manganese dioxide nanorods nanocomposite as an electrode material for supercapacitors

Co3O4/carbon Nano-Onions Composite As Supercapacitor Electrode and Its Excellent Electrochemical Performance

Graphene-cerium Oxide/porous Polyaniline Composite As a Novel Electrode Material for Supercapacitor

Synthesis of biochemically reduced graphene-oxide/Fe0 containing polyaniline ternary hybrid composite through interfacial polymerization for supercapacitors

Hydrothermal Synthesis of Polyaniline Nanospheres Coupled with Graphene Oxide for Enhanced Specific Capacitance Performances

Polyaniline/SnO2 nanocomposite for supercapacitor applications